To improve the adsorption selectivity towards hexavalent chromium anion (Cr(VI)), surface Cr(VI)-imprinted polypropylene (PP) fibers were fabricated by the plasma-mediated grafting strategy. Hence, a non-thermal Rradio frequency discharge plasma irradiation followed by a gaseous phase grafting was used to load acrylic acid (AA) onto PP fibers, which was afterwards amidated with triethylenetetramine and subjected to imprinting with a Cr(VI) template. The plasma irradiation conditions, i.e., gas species, output power, pressure, and time, were optimized and then the influence of grafting time, pressure, and temperature on the grafting degree of AA was investigated. Scanning electron microscopy and Fourier transform infrared spectroscopy were used for the characterization of pristine and modified fibers and to confirm the synthesis success. The hydrophilicity of modified fibers was greatly improved compared with pristine PP fibers. The adsorption thermodynamics and kinetics of Cr(VI) were investigated, as well as the elution efficiency and reusability. The prepared imprinted fibers showed superior adsorption selectivity to Cr(VI) compared with non-imprinted fibers. Finally, the stability of the imprinted fibers against the oxidation ability of Cr(VI) is discussed.

This paper uses polypropylene (PP) as the matrix and acrylic acid (AA) and maleic anhydride (MAH) as functional monomers to prepare PP-g-(AA-MAH) fibers by suspension grafting and melt-blown spinning technology that are easy to industrially scale-up. The fibers can be used to adsorb aniline. Results showed that the grafting ratio reached the maximum of 12.47%. The corresponding optimal conditions were grafting time of 3 h, AA: MAH = 0.75, total monomer content of 55%, benzoyl peroxide 1.4%, xylene concentration of 6 mL/g PP, and deionized water content of 8 mL/g PP. Owing to its good fluidity and thermal stability, the product of suspension grafting can be used for melt-blown spinning. Infrared spectroscopic and nuclear magnetic resonance spectroscopic analyses indicated that AA and MAH were successfully grafted onto PP fibers. After grafting, the hydrophilicity of PP-g-(AA-MAH) fiber increased. Therefore, it had higher absorptivity for aniline and the adsorption capacity could reach 42.2 mg/g at 45 min and pH = 7. Moreover, the PP-g-(AA-MAH) fibers showed good regeneration performance.