Three-dimensional (3D) printing has allowed for the production of geometrically complex 3D objects with extreme flexibility, which is currently undergoing rapid expansion in terms of materials, functionalities, as well as areas of application. When attempting to print 3D microstructures in glass, femtosecond laser-induced chemical etching (FLICE)—which is a subtractive 3D printing technique—has proved itself a powerful approach. Here, we demonstrate the fabrication of macro-scale 3D glass objects of large heights up to ~3.8 cm with an identical lateral and longitudinal feature size of ~20 μm. The remarkable accomplishment is achieved by revealing an unexplored regime in the interaction of ultrafast laser pulses with fused silica, which results in depth-insensitive focusing of the laser pulses inside fused silica.

We demonstrate a microfluidic mixer of high mixing efficiency in fused silica substrate using femtosecond laser-induced wet etching and hydroxide-catalysis bonding method. The micromixer has a three-dimensional geometry, enabling efficient mixing based on Baker’s transformation principle. The cross-sectional area of the fabricated micromixer was 0.5 × 0.5 mm², enabling significantly promotion of the throughput of the micromixer. The performance of the fabricated micromixers was evaluated by mixing up blue and yellow ink solutions with a flow rate as high as 6 mL/min.