Organophilic clay particles were added to a standard intumescent formulation and, since the role of clay expansion or intercalation is still a matter of much controversy, several clays with varying degrees of interlayer distances were evaluated. The composites were obtained by blending the nanostructured clay and the intumescent system with a polyethylenic copolymer. The flame-retardant properties of the materials were evaluated by the limiting oxygen index (LOI), the UL-94 rating and thermogravimetric analysis (TGA). The results showed that the addition of highly expanded clays to the ammonium polyphosphate and pentaerythritol formulation does not significantly increase the flame retardancy of the mixture, when measured by the LOI and UL-94. However, when clays with smaller basal distances were added to the intumescent formulation, a synergistic effect was observed. In contrast, the simple addition of clays to the copolymer, without the intumescent formulation, did not increase the fire retardance of the materials.

The aim of this study is the evaluation of partially sulfonated polystyrene nanoparticles (SPSNP) efficiency as nanocarriers for a non-ionic surfactant, oleic acid diethanolamide (OADA), in the reduction of the surfactant losses and the increase of oil recovery. The synthesized oleic acid diethanolamide was characterized by FTIR, ¹H NMR, ¹³C NMR, surface tension (γ = 36.6 mN·m⁻¹, CMC = 3.13 × 10⁻⁴ M) and interfacial tension of mineral oil/OADA aqueous solutions (IFT_eq = 0.07 mN·m⁻¹). The nanoparticles (SPSNP) were obtained by emulsion polymerization of styrene, DVB and sodium 4-styrenesulfonate (St-S) in the presence of OADA aqueous solution and were characterized by FTIR and PCS. The results show that the presence of ionic groups in the polymer structure promoted a better nanoparticles suspensions′ stability, smaller particles production and more pronounced IFT reduction. The SPSNP obtained with an OADA concentration twenty times its CMC and 0.012 mol % of St-S presented a particle size around 66 nm and can act as efficient nanocarriers decreasing the water/oil interfacial tension to low values (0.07 mN·m⁻¹) along the time, when in contact with the oil. Transport and oil recovery tests of the nanocarriers systems in an unconsolidated sand porous medium test show that the SPSNP do inhibit surfactant adsorption onto sand particles surface and induced an increase of oil recovery of up to about 13% relative to the water flooding oil recovery, probably due to a synergistic effect between the nanoparticles and surfactant action at the water/oil interface.