The present work was aimed to study the friction and wear behaviour of graphene nanoplatelets (GNPs) under extreme pressure conditions as an anti-weld additive for neem oil. The effect of neem oil, blended with various loading of GNPs on the friction and wear characteristics has been investigated. From the experimental results, it was found that 1 wt.% of GNPs in neem oil showed the least coefficient of friction and smoother wear scar diameter. The extreme pressure test was performed on neem oil with and without GNPs as per ASTM standards. The extreme pressure test results indicated the improvement in seizure load of neem oil by 27.8% at 0.5 wt.% of GNPs as compared to pure neem oil. Optical microscopy of worn steel ball surface revealed the pit formation and the formation of wedge cutting edge in GNPs modified neem oil.

Various amounts of short fibers (glass and carbon) and particulate fillers like polytetrafluoroethylene (PTFE), silicon carbide (SiC), and alumina (Al₂O₃) were systematically introduced into the thermoplastic copolyester elastomer (TCE) matrix for reinforcement purpose. The mechanical properties such as storage modulus, loss modulus, and Tanδby dynamic mechanical analysis (DMA) and three-body abrasive wear performance on a dry sand rubber wheel abrasion tester have been investigated. For abrasive wear study, the experiments were planned according toL27orthogonal array by considering three factors and three levels. The complex moduli for TCE hybrid composites were pushed to a higher level relative to the TCE filled PTFE composite. At lower temperatures (in the glassy region), the storage modulus increases with increase in wt.% of reinforcement (fiber + fillers) and the value is maximum for the composite with 40 wt.% reinforcement. The loss modulus and damping peaks were also found to be higher by the incorporation of SiC and Al₂O₃microfillers. The routine abrasive wear test results indicated that TCE filled PTFE composite exhibited better abrasion resistance. Improvements in the abrasion resistance, however, have not been achieved by short-fiber and particlaute filler reinforcements. From the Taguchi’s experimental findings, optimal combination of control factors were obtained for minimum wear volume and also predictive correlations were proposed. Further, the worn surface morphology of the samples was discussed.