In this study, biodegradable slow-release fertilizer (SRF) hydrogels were synthesized from hydroxyl propyl methyl cellulose (HPMC), polyvinyl alcohol (PVA), glycerol and urea (SRF1) and HPMC, PVA, glycerol, urea and blended paper (SRF2). The fertilizer hydrogels were characterized by SEM, XRD and FTIR. The swelling capacity of the hydrogels in both distilled and tap water as well as their water retention capacity in sandy soil were evaluated. The hydrogels had good swelling capacity with maximum swelling ratio of 17.2 g/g and 15.6 g/g for SRF1 and SRF2 in distilled, and 14.4 g/g and 15.2 g/g in tap water, respectively. The water retention capacity of the hydrogels in sandy soil exhibited higher water retention when compared with soil without the (SRFs). The soil with the hydrogels was found to have higher water retention than the soil without the hydrogels. The slow-release profile of the hydrogels was also evaluated. The result suggested that the prepared fertilizer hydrogels has a good controlled release capacity. The blended paper component in SRF2 was observed to aid effective release of urea, with about 87.01% release in soil at 44 days compared to the pure urea which was about 97% release within 4 days. The addition of blended paper as a second layer matrix was found to help improve the release properties of the fertilizer. The swelling kinetic of the hydrogel followed Schott’s second order model. The release kinetics of urea in water was best described by Kormeye Peppas, suggesting urea release to be by diffusion via the pores and channels of the SRF, which can be controlled by changing the swelling of the SRF. However, the release mechanism in soil is best described by first order kinetic model, suggesting that the release rate in soil is depended on concentration and probably on diffusion rate via the pores and channels of the SRF.

Pelletization from nonwoody biomass has gained a lot of attention due to its potential to secure biomass feedstock supply and pricing. Studies have been conducted to produce biopellets from different parts of Napier grass plant. In this study, two different species of Napier grass were used. Two pressure points and five different times were varied accordingly. Proximate, ultimate, and Fourier transform infrared spectroscopy (FTIR) analyses were performed to assess chemical properties. Statistical analysis of the collected data validated and supported the discussion. The produced pellets of Napier grass exhibited good energy density comparable to those in the literature based on gross calorific values. The pellet density demonstrated a significant effect with time, pressure, and feedstock ratios. The pellet durability test showed comparable characteristics to another biomass pellet. Both Pakchong Napier grass (PNG) and wild Napier grass (WNG) biopellet densities obtained were higher than 0.650 g/cm³, and the durability was higher than 95%. This signifies that the pellet can withstand repeated transfer during handling without breakage.

The catalytic and non-catalytic pyrolytic conversion kinetics of palm kernel shell with untreated (as received) and H₂SO₄ treated coal bottom ash as catalyst were investigated in this study. The activation energy was determined using Flynn-Wall-Ozawa (FWO) kinetic model and distributed activation energy model (DEAM) isoconversional kinetic models. The study was conducted using thermogravimetric analysis at 10, 20, 30 and 50 °C/min heating rates. The activation energy (E_a) ranged from 145.7-228.3 kJ/mol and 142.1-274.2 kJ/mol for FWO and DEAM, respectively. The use of acid treated ash reduced the activation energy compared to the non-catalytic process while the untreated ash increased the activation energy.