In this work, the meso-tetra[4-(2-(3-n-pentadecylphenoxy)ethoxy]phenylporphyrin (H₂P), obtained from the cashew nut shell liquid (CNSL), and its zinc (ZnP) and copper (CuP) metallic complexes, were applied as emitting layers in organic light emitting diodes (OLEDs). These compounds were characterized via optical and electrochemical analysis and the electroluminescent properties of the device have been studied. We performed a cyclic voltammetry analysis to determine the Highest Occupied Molecular Orbital (HOMO) and Lowest Unoccupied Molecular Orbital (LUMO) energy levels for the porphyrins, in order to select the proper materials to assemble the device. H₂P and ZnP presented fluorescence emission band in the red region, from 601 nm to 718 nm. Moreover, we verified that the introduction of bulky substituents hinders the π–π stacking, favoring the emission in the film. In addition, the strongest emitter, ZnP, presented a threshold voltage of 4 V and the maximum irradiance of 10 μW cm⁻² with a current density (J) of 15 mA cm⁻² at 10 V. The CuP complex showed to be a favorable material for the design of OLEDs in the infrared. These results suggest that the porphyrins derived from a renewable source, such as CNSL, is a promising material to be used in organic optoelectronic devices such as OLEDs.

In this work we report the synthesis of new hybrid nanomaterials in the core/shell/shell morphology, consisting of a magnetite core (Fe₃O₄) and two consecutive layers of oleic acid (OA) and phthalocyanine molecules, the latter derived from cashew nut shell liquid (CNSL). The synthesis of Fe₃O₄ nanoparticle was performed via co-precipitation procedure, followed by the nanoparticle coating with OA by hydrothermal method. The phthalocyanines anchorage on the Fe₃O₄/OA core/shell nanomaterial was performed by facile and effective sonication method. The as obtained Fe₃O₄/OA/phthalocyanine hybrids were investigated by Fourier transform infrared spectroscopy, X-ray diffraction, UV-visible spectroscopy, transmission electron microscopy (TEM), thermogravimetric analysis and magnetic measurements. TEM showed round-shaped nanomaterials with sizes in the range of 12–15 nm. Nanomaterials presented saturation magnetization (Ms) in the 1–16 emu/g and superparamagnetic behavior. Furthermore, it was observed that the thermal stability of the samples was directly affected by the insertion of different transition metals in the ring cavity of the phthalocyanine molecule.