Chemical doping with foreign atoms is an effective method to intrinsically modify the properties of the host materials. In this paper, we report a facile strategy to prepare nitrogen and boron doped monolayer graphene by using urea and boric acid as solid precursors. By adjusting the elemental precursors, the nitrogen content could be modulated from 0.9 to 4.8% for nitrogen doped graphene and the boron content from 0.7 to 4.3% for boron doped graphene respectively, as estimated by X-ray photoelectron spectroscopy. The mobilities of the nitrogen and boron doped graphene-based back-gate field-effect transistors are about 350–550 cm² V⁻¹ s⁻¹ and 450–650 cm² V ⁻¹ s⁻¹ respectively. Our results are better than plasma treated nitrogen and boron doped graphene. Therefore the synthesis of nitrogen and boron doped graphene sheets by a solid doping elemental precursor method is considered to be an efficient approach to producing graphene with excellent optical and electrical performances at relatively low cost.

Carbon dots (CDs) are synthesized by the solvothermal method with four kinds of solvents including water, dimethylformamide (DMF), ethanol, and acetic acid (AA). The aqueous solutions of the above CDs emit multiple colors of blue (470 nm), green (500 nm), yellow (539 nm), and orange (595 nm). The structures, sizes, and chemical composition of the CDs are characterized by transmission electron microscopy (TEM), dynamic light scattering (DLS), X-ray diffraction (XRD), Fourier transform infrared (FTIR), and X-ray photoelectron spectroscopy (XPS). The optical properties of multicolored CDs are analyzed by UV–vis absorption and photoluminescence (PL) spectra. It has been revealed that DMF is the key solvent to synthesized CDs for the red shift of fluorescence emission, which could be enhanced by adding an AA solvent. The structures of functional groups such as the contents of graphitic N in carbon cores and oxygen-containing functional groups on the surface of CDs are affected by these four solvents. According to the oxidation and selective reduction of NaBH₄, the implication for multicolor imaging has been discussed based on the COOH, C–O–C, and C═O functional groups.