Objectives: The aim of the present work was to comparatively investigate the generation and characteristics of fretting and sliding wear debris produced by CuNiAl against 42CrMo4. Methods: Tribological tests were conducted employing a self-developed tribometer. Most experimental conditions were set the same except for the amplitudes and number of cycles. Morphological, chemical, microstructural and dimensional features of the worn area and debris were investigated using optical microscope (OM), X-ray diffraction (XRD), scanning electron microscopy (SEM) with energy dispersive spectroscopy (EDS) and a laser particle sizer. Outcomes: Not only wear scar profiles but also the wear debris color, distribution and generated amount under fretting and sliding wear modes were quite different, which can be attributed to the significant difference in wear mechanisms. Particle size analysis indicates that the fretting debris has a smaller size distribution range; the biggest detected fretting and sliding wear debris sizes were 141 μm and 355 μm, respectively. Both fretting and sliding debris are mainly composed of copper and its oxides, but the former shows a higher oxidation degree.

This paper investigates the effect of ultrasonic surface rolling (USR) on the fretting wear properties of the 7075 aluminum alloy. A white light interferometer, Vickers hardness tester, and X-ray diffractometer were employed to comparatively analyze the variations in surface roughness, hardness. and grain size before and after the USR treatment. The fretting tests were carried out under oil lubricated and dry fretting conditions, using a ball-on-flat contact tangential fretting tester. The worn surface morphology, wear debris, and chemical composition were analyzed using an optical microscope (OM), a scanning electron microscope (SEM), and X-ray photoelectron spectroscopy (XPS), etc. The results revealed that after USR treatment, the surface roughness was reduced by 90%, the hardness was increased by 13HV, and the grains were refined. Moreover, the wear was reduced under oil lubrication conditions but increased under dry fretting conditions. It can be concluded that the microstructure and mechanical properties of the 7075 aluminum alloy surface can be enhanced by the USR treatment. The improved fretting performance in oil should be attributed to the increased surface hardness, which helps reduce abrasive wear and plastic deformation. However, under dry fretting conditions, the wear was increased due to the presence of hard debris particles that peel off from the USR-treated surface, leading to aggravated abrasion.

Friction conditions significantly impact the temperature and phases of titanium forged parts, further directly affecting the microstructures and mechanical properties of final parts. In this paper, a 2D simplified finite element (FE) model combined with phase transition equations is developed to simulate a Ti-6Al-4V drum forging procedure. Then, friction effects on the temperature and phases of the forged drum are numerically analyzed and verified by experiments. The simulated results indicate that a reasonable range of friction factor is needed to obtain a relatively homogenous temperature distribution within the forged drum. Moreover, unlike its small influence on the α + β phase, improving friction obviously decreases the general levels of temperature and β phase and increases the homogeneities of α and β phases within the forged drum, which are associated with cooling rates and the heating effects of friction and deformation.