Starch-based hydrogels have received considerable interest due to their safe nature, biodegradability and biocompatibility. The aim of this study was to verify the possibility of producing natural hydrogels based on potato starch by high hydrostatic pressure (HHP), identifying suitable processing conditions allowing to obtain stable hydrogels, as well as to characterize structural and mechanical properties of these products. Sieved (small size granules and medium size granules) and unsieved potato starch samples were used to prepare aqueous suspensions of different concentrations (10–30% w/w) which were processed at 600 MPa for 15 min at different temperatures (25, 40 and 50 °C). Products obtained were characterized by different techniques (light and polarized microscopy, Fourier transform infrared spectroscopy (FTIR), rheology and differential scanning calorimetry (DSC)). Results obtained so far demonstrated that potato starch suspensions (20% starch–water concentration (w/w)) with granules mean size smaller than 25 µm treated at 600 MPa for 15 min and 50 °C showed a complete gelatinization and gel-like appearance. Potato HHP hydrogels were characterized by high viscosity, shear-thinning behavior and a highly structured profile (G’ >> G’’). Moreover, their FTIR spectra, similarly to FTIR profiles of thermal gels, presented three absorption bands in the characteristic starch-gel region (950–1200 cm⁻¹), whose intensity increased with decreasing the particle size and increasing the processing temperature. In conclusion, potato starch hydrogels produced by HHP in well-defined processing conditions exhibited excellent mechanical properties, which can be tailored according to the requirements of the different applications envisaged.

In this study, the effects of the amylose/amylopectin content on starch gelation and the physical characteristics of hydrogels produced by HPP were studied by optical and rheological measurements in steady-state conditions. Additionally, the effects of the storage temperature (4 °C and 20 °C) and type of packaging (plastic bags or sealed Petri dishes) on the physical stability of the hydrogels were evaluated for 30 days of storage by evaluating the shrinkage of the granules, as well as the weight loss, water activity, organoleptic, and rheological properties. The experimental findings suggested that amylose plays an antagonistic role in determining the capacity of the starch granules to absorb water under pressure and to create stable and structured gels and on the physical stability of hydrogels due to its influence over the starch retrogradation extent during storage. Twenty per cent amylose was the minimum concentration to form stable corn starch HPP hydrogels with good physical and rheological properties. Moreover, a storage temperature of 20 °C and the use of polymeric bags were evaluated as the most suitable storage conditions and packaging materials enabling the long storage of corn starch hydrogels.

Starch-based hydrogels are natural polymeric structures with high potential interest for food, cosmeceutical, and pharmaceutical applications. In this study, the physical stability of starch-based hydrogels produced via high-pressure processing (HPP) was evaluated using conventional and accelerated methods. For this purpose, conventional stability measurements, namely swelling power, water activity, texture, and organoleptic properties, as well as microbiological analysis of rice, corn, wheat, and tapioca starch hydrogels, were determined at different time intervals during storage at 20 °C. Additionally, to assess the stability of these structures, accelerated tests based on temperature sweep tests and oscillatory rheological measurements, as well as temperature cycling tests, were performed. The experimental results demonstrated that the physical stability of starch-based HPP hydrogels was interdependently affected by the microorganisms’ action and starch retrogradation, leading to both organoleptic and texture modifications with marked reductions in swelling stability and firmness. It was concluded that tapioca starch hydrogels showed the lowest stability upon storage due to higher incidence of microbial spoilage. Accelerated tests allowed the good stability of HPP hydrogels to be predicted, evidencing good network strength and the ability to withstand temperature changes. Modifications of the rheological properties of corn, rice, and wheat hydrogels were only observed above 39 °C and at stress values 3 to 10 times higher than those necessary to modify commercial hydrogels. Moreover, structural changes to hydrogels after cycling tests were similar to those observed after 90 days of conventional storage. Data obtained in this work can be utilized to design specific storage conditions and product improvements. Moreover, the accelerated methods used in this study provided useful information, allowing the physical stability of starch-based hydrogels to be predicted.