Dye-sensitized solar cells (DSSCs) were assembled by using the bougainvillea flowers, red turnip and the purple wild Sicilian prickly pear fruit juice extracts as natural sensitizers of TiO₂ films. The yellow orange indicaxanthin and the red purple betacyanins are the main components in the cocktail of natural dyes obtained from these natural products. The best overall solar energy conversion efficiency of 1.7% was obtained, under AM 1.5 irradiation, with the red turnip extract, that showed a remarkable current density (Jsc = 9.5 mA/cm²) and a high IPCE value (65% at λ = 470 nm). Also the purple extract of the wild Sicilian prickly pear fruit showed interesting performances, with a Jsc of 9.4 mA/cm², corresponding to a solar to electrical power conversion of 1.26%.

Solution-processed graphene and related two-dimensional materials enable the next-generation photovoltaics.

Here we report on the fabrication of a new low-cost transparent cathode based on platinum nanoparticles prepared by a bottom-up synthetic approach. Scanning Electron Microscope (SEM) images showed the platinum nanoparticles homogeneously distributed on a fluorine doped tin oxide conductive glass surface. We demonstrated that, with such a type of cathode, the solar energy conversion efficiency is the same as that obtained with a platinum sputtered counter-electrode, and is more than 50% greater than that obtained with a standard electrode, i.e. one prepared by chlorine platinum acid thermal decomposition, in similar working conditions. Using a special back-reflecting layer of silver, we improved upon the performance of a counter-electrode based on platinum sputtering, achieving an overall solar conversion efficiency of 4.75% at 100 mW cm⁻² (AM 1.5) of simulated sunlight.

Seven flavylium salt dyes were employed for the first time as sensitizers for dye-sensitized solar cells (DSSCs). The theoretical and experimental wavelengths of the maximum absorbances, the HOMO and LUMO energy levels, the coefficients, the oscillator strengths and the dipole moments are calculated for these synthetic dyes. The introduction of a donor group in the flavylium molecular structure was investigated. Photophysical and photoelectrochemical measurements showed that some of these synthetic analogues of anthocyanins are very promising for DSSC applications. The best performance was obtained by a DSSC based on the novel compound 7-(N,N-diethylamino)-3′,4′-dihydroxyflavylium which produced a 2.15% solar energy-to-electricity conversion efficiency, under AM 1.5 irradiation (100 mW cm⁻²) with a short-circuit current density (J_sc) of 12.0 mA cm⁻², a fill factor of 0.5 and an open-circuit voltage (V_oc) of 0.355 V; its incident photocurrent efficiency of 51% at the peak of the visible absorption band of the dye is remarkable. Our results demonstrated that the substitution of a hydroxylic group with a diethylamine unit in position 7 of ring A of the flavylium backbone expanded the π-conjugation in the dye and thus resulted in a higher absorption in the visible region and is advantageous for effective electron injection from the dye into the conduction band of TiO₂.

Bifacial solar cells (BFSCs) are designed to enhance electrical power generation per unit area compared to traditional monofacial cells. They accomplish this by capturing sunlight from both the front and rear surfaces.