Perlite is a volcanic glass that, under thermal treatment, expands, producing a highly porous and lightweight granular material which finds application in the construction, horticulture, insulation and other industrial sectors. Proper control of the feed properties and the expansion conditions allows the production of purpose-oriented grades, while the primary evaluation of its appropriateness for use in each sector is performed by the proper characterization of relevant physical, thermal or/and mechanical properties. However, due to its extreme fineness, low density, and friability, most of the available characterization methods either fail in testing or provide erroneous results, while for certain properties of interest, a method is still missing. As a consequence, the way towards the evaluation of the material is rife with uncertainties, while a well-defined methodology for the characterization of the critical properties is of practical importance towards the establishment of a pathway for its proper analysis and assessment. This article presents the available methodology for determining the main properties of interest, i.e., the size and density, water repellency/absorption and oil absorption, the microstructural composition, crushing and abrasion resistance and isostatic crushing strength, and also sampling and size reduction processes. The issues raised by the application of existing methods are analyzed and discussed, ending up to a proper methodology for the characterization of each property, based on the long-term experience of the Perlite Institute. The study is supplemented by updated insights on ore genesis, physicochemical properties, mineralogical composition and the expansion mechanism, as background information for the sufficient comprehension of the nature and properties of perlite.

The use of amorphous microspheres as filler in composites is promising due to their light weight, low cost, incombustibility, and the ability to alter relevant properties of the final composite. Contrary to glass spheres, perlite microspheres are much cheaper and can be tailor-made to facilitate purpose-oriented alteration of the final composite. We report the use of perlite microspheres for the preparation of: (1) composites, through a compression molding (hot pressing) technique; and (2) composite filaments, in a single screw extruder, as well as their use for sample printing through Fused Deposition Modeling (FDM). Proper characterization of the produced composites allows for their evaluation in terms of physical, thermal, and mechanical properties and with regards to the manufacturing technique, the filler fraction, and size. Composite samples of acceptable quality in terms of filler survival and dispersion as well as mechanical properties were produced through compression molding using fine expanded perlite microspheres (<90 μm) up to an infill ratio of 40 vol.%. Fine fillers (<90 μm) performed well in FDM, allowing printing of composite dogbone samples with a higher Young’s modulus and elongation and similar ultimate tensile strength compared to benchmark, up to an infill ratio of 20 vol.%. Composite samples present a slightly lower burning rate compared to those produced solely by ABS. Perlite microspheres present good workability in both applications, possessing satisfactory performance as filler in the composites, and can thus be assumed a promising multifunctional filler for various thermoplastics considering their low price, environmental impact, and fire rating.

Expanded perlite constitutes one of the most competitive insulating materials that is widely used in construction and manufacturing industry due to its unique properties combination; it is white, natural, lightweight, chemically inert, and exhibits superior insulating properties (thermal and acoustic) and fire resistance. Conventionally, perlite expansion is performed in vertical gas-fired furnaces; the conventional perlite expansion process has certain disadvantages which affect expanded products quality, thus limiting their performance and range of applications. In order to overcome the drawbacks of the conventional expansion technique, a new perlite expansion process has been designed based on a vertical electrical furnace (VEF). In the current study, fine perlite samples (-150 μm) from Milos Island, Greece, were expansed in the novel VEF and a conventional gas-fired furnace with the aim to evaluate and compare the main physical properties of the expanded products. The novel expanded perlite particles were characterised by superior properties, namely increased compression strength, competitive water and oil absorption capability, size homogeneity, spherical shape and decreased surface porosity in comparison to conventionally expanded samples.