Microstructured optical fibers can be precisely tailored for many different applications, out of which sensing has been found to be particularly interesting. However, placing silica optical fiber sensors in harsh environments results in their quick destruction as a result of the hydrolysis process. In this paper, the degradation mechanism of bare and metal-coated optical fibers at high temperatures under longitudinal strain has been determined by detailed analysis of the thermal behavior of silica and metals, like copper and nickel. We furthermore propose a novel method of enhancing the lifetime of optical fibers by the deposition of electroless nickel-phosphorous alloy in a low-temperature chemical process. The best results were obtained for a coating comprising an inner layer of copper and outer layer of low phosphorous nickel. Lifetime values obtained during the annealing experiments were extrapolated to other temperatures by a dedicated model elaborated by the authors. The estimated copper-coated optical fiber lifetime under cycled longitudinal strain reached 31 h at 450 °C.

We investigate the influence of air holes on phase sensitivity in microstructured optical fibers to longitudinal strain. According to the numerical simulations performed, large air holes in close proximity to a fiber core introduce significant compression stress to the core, which results in an increase in the effective refractive index sensitivity to longitudinal strain. The theoretical investigation is verified by an experiment performed on four fibers drawn from the same preform and differentiated by air hole diameter. We show that introducing properly designed air holes can lead to a considerable increase in normalized effective refractive index sensitivity to axial strain from −0.21 ε⁻¹ (for traditional single mode fiber) to −0.14 ε⁻¹.