This article reviews the recent advances and various factors affecting the improvement of the biological properties of calcium phosphate for bone repair.

Properties of chitosan/polymer and chitosan/bioceramic composite scaffolds for articular cartilage defect repair are reviewed.

In this study, Co-based laser cladding coatings reinforced by multiple phases were fabricated on titanium alloy. Co42 Co-based self-fluxing alloy, B₄C, and CeO₂ mixed powders were used as the precursor materials. The coatings were mainly composed of γ-Co/Ni, CoTi₂, CoTi, NiTi, TiC, Cr₇C₃, TiB₂, and TiB phases. A typical TiB₂/Cr₇C₃/TiC composite structure was chosen. It was found that CeO₂ did not influence the phase types of the coating significantly, but was effective in refining the microstructure and enhancing the microhardness and dry sliding wear resistance. Compared with the Ti-6Al-4V titanium alloy, the microhardness and wear resistance of the composite coatings were enhanced by 3.44–4.21 times and 14.26–16.87 times, respectively.