Functionalities of 3D printing filaments have gained much attention owing to their properties for various applications in the last few years. Innovative biocomposite 3D printing filaments based on polylactic acid (PLA) composited with ZnO nanoflowers at varying contents were successfully fabricated via a single-screw extrusion technique. The effects of the varying ZnO nanoflower contents on their chemical, thermal, mechanical, and antibacterial properties were investigated using Fourier transform infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), and tensile testing, as well as qualitative and quantitative antibacterial tests, respectively. It was found that the ZnO nanoflowers did not express any chemical reactions with the PLA chains. The degrees of the crystallinity of the PLA/ZnO biocomposite filaments increased when compared with those of the neat PLA, and their properties slightly decreased when increasing the ZnO nanoflower contents. Additionally, the tensile strength of the PLA/ZnO biocomposite filaments gradually decreased when increasing the ZnO nanoflower contents. The antibacterial activity especially increased when increasing the ZnO nanoflower contents. Additionally, these 3D printing filaments performed better against Gram-positive (S. aureus) than Gram-negative (E. coli). This is probably due to the difference in the cell walls of the bacterial strains. The results indicated that these 3D printing filaments could be utilized for 3D printing and applied to medical fields.

Natural rubber (NR) composites filled with silica are typically used for tire tread applications owing to their low energy consumption and low rolling resistance. Tire tread properties vary broadly depending on the compound formulation and curing conditions. Silica loading is recognized as a critical factor influencing the mechanical properties of the composites. In this work, we aim to investigate the effect of silica loading (10–50 phr) on the mechanical properties of NR composites. Silica was prepared from rice husk waste via chemical treatment and subsequent calcination at 600 °C. Prior to the compound mixing process, silica was modified by a silane coupling agent to improve compatibility with the NR matrix. The NR compounds reinforced with silane-modified silica from rice husk were prepared using a two-roll mill machine. The scorch and cure times increased as the silica loading increased. The mechanical properties of the NR composites, including tensile strength, elongation at break, modulus, hardness, and abrasion loss, were examined as a function of silica loading. Tensile strength increased and reached the maximum value at 20 phr but decreased at high loading owing to the agglomeration of silica in the NR matrix. With increasing silica loading, hardness and modulus increased, whereas elongation at break and abrasion resistance decreased slightly. These results indicate that NR composites filled with silica are stiffer and harder at a higher silica loading due to the strong interaction between silica and the NR matrix, inhibiting the segmental mobility of rubber chains. We anticipate that the compound formulation presented in this work could potentially be adapted to tire tread applications.

N,N-bis(2-hydroxybenzyl)alkylamines, benzoxazine dimers, are the major product produced from benzoxazine monomers on mono-functional phenol by the one step ring opening reaction. Due to the metal responsive property of benzoxazine dimers, in this present work, N,N-bis(5-methyl-2-hydroxybenzyl)methylamine (MMD), N,N-bis (5-ethyl-2-hydroxybenzyl)methylamine (EMD), and N,N-bis(5-methoxy-2-hydroxybenzyl) methyl amine (MeMD), are considered as novel ligands for rare earth metal ion, such as cerium(III) ion. The complex formed when the clear and colorless solutions of cerium nitrate and benzoxazine dimers were mixed, results in a brown colored solution. The metal-ligand ratios determined by the molar ratio and the Job’s methods were found to be in a ratio of 1:6. To clarify the evidence of the complex formation mechanism, the interactions among protons in benzoxazine dimers both prior to and after the formation of complexes were determined by means of ¹H-NMR, 2D-NMR and a computational simulation. The single phase ceria (CeO₂) was successfully prepared by thermal decomposition of the Ce(III)-benzoxazine dimer complexes at 600 °C for 2 h, was then characterized using XRD. In addition, the ceria powder investigated by TEM is spherical with an average diameter of 20 nm.