Based on the Ø195 mm round bloom continuous casting of oil pipe steel, a two dimensional thermal-mechanical coupled model has been developed to investigate the deformation behavior of round bloom during soft reduction (SR) in the reduction force mode. Good agreement was achieved in surface temperature, shell thickness and contact zone width from modeling and measurement. Under the same reduction force, the reduction amount of round bloom at the front unit is much larger than back unit. Moreover, due to its higher temperature and lower center solid fraction, the deformation penetration before solidification is much stronger than that after solidification. Considering the limitation of the round bloom ovality, the maximum allowable force in reduction unit is calculated. According to the simulation results, a multi-unit soft reduction plan was proposed and carried out on the Ø195 mm round bloom. After the reduction process of No.1 to No.3 withdrawal units, the shrinkage porosity in the center of the round bloom was almost vanished, while the number and size of spot segregation were significantly reduced. Moreover, the oil pipe produced by the round bloom with SR got a better resistance to sulfide stress corrosion (SSC). It indicates that SR is an effective technology for the round bloom to control the shrinkage porosity and spot segregation in the continuous casting.

C110 oil well casing tubes should have high strength and corrosion resistance which is commonly used for deep wells operation containing corrosive media. In this paper, the microstructure evolution of a kind of semi-macro segregation originated banded structure in casing tubes is studied under different heat treatments. It is shown that the characteristics of the banded structure will change significantly in subsequent hot working and heat treatment processes. For the hot-rolled ones, the banded structure is composed of pearlite plus bainite. After quenching, it evolves into martensite band with high concentration solute elements. Finally, the banded structure will change into a carbide banding under the following tempering process. The temperature and cooling rate of the tempering practice show an obvious effect on the final band structure. To improve anti-SSC (sulfide stress corrosion cracking) performance, the favorable QT (quenching and tempering) practice for C110 steel should be a higher tempering temperature and a quicker cooling rate, from which the banded structure defects can be decreased together with an obvious improvement of the tube wall hardness uniformity.

The effect of strain aging on the microstructure, including copper precipitation, and mechanical properties of an industrially produced Cu-containing microalloyed low carbon pipeline steel has been investigated. The precipitation of round bcc-Cu particles with diameters of ∼7 nm has been clearly observed in the microstructure after strain aging. The strength of pipeline steel significantly increased while the elongation and impact toughness did not apparently decrease. Unlike welded pipe, few carbon atoms in supersaturated solid solution diffuse to the mobile dislocations, forming Cottrell atmospheres and producing strain aging phenomenon in seamless pipe. This difference is attributed to the different pipe making technique: thermo mechanically controlled processed for welded pipe and traditional heat-treatment for seamless pipe.

Stress corrosion cracking (SCC) behaviour of 316L stainless steel in CO₂–H₂S–Cl⁻ environments with and without methyldiethanolamine (MDEA) was investigated by slow strain rate testing and scanning electron microscopy (SEM). The results show that elongation ratio, reduction in area ratio (RAR) and time to failure ratio (TTFR) of 316L stainless steel were low in CO₂–H₂S–Cl⁻ environments. The corresponding fractography exhibited flat brittle fracture with quasi-cleavage pattern, indicative of high SCC susceptibility. Hydrogen penetration and corrosion pits could be responsible for the high SCC susceptibility of 316L stainless steel in this condition. For the CO₂–H₂S–Cl⁻ environments in the presence of MDEA, 316L stainless steel possessed high ER, RAR and TTFR (nearly 100%). High SCC resistance of 316L stainless steel could be associated with MDEA induced removal of H₂S/CO₂ and absorption on the steel surface.

The influence of tempering temperature on the microstructure of 0.5Cr0.4W steels was investigated by scanning electron microscope, and the roles of grain boundary character, dislocation, and Taylor factor in sulfide stress cracking (SSC) resistance were interpreted using the election backscattered diffraction technique. The 0.5Cr0.4W steels tempered at 690 °C, 700 °C, and 715 °C all showed tempered martensites. The specimen tempered at 715 °C exhibited a higher critical stress intensity factor (K_ISSC) of 34.58 MPa·m^0.5, but the yield strength of 800 MPa did not meet the criterion of 125 ksi (862 MPa) grade. When the specimen was tempered at 690 °C, the yield strength reached 960 MPa and the K_ISSC was only 21.36 MPa·m^0.5, displaying poorer SSC resistance. The 0.5Cr0.4W steel tempered at 700 °C showed a good combination of yield strength (887 MPa) and SSC resistance (K_ISSC: 31.16 MPa·m^0.5). When increasing the tempering temperature, the local average misorientation and Taylor factor of the 0.5Cr0.4W steels were decreased. The reduced dislocation density, and greater number of grains amenable to slippage, produced less hydrogen transport and a lower crack sensitivity. The SSC resistance was, thus, increased, owing to the minor damage to hydrogen aggregation. Therefore, 700 °C is a suitable tempering temperature for 0.5Cr0.4W casing steel.

The effect of Ti and B microalloying on the hardenability, prior austenite grain size (PAGS), mechanical properties, and sulfide stress cracking (SSC) of C110 grade steel was studied by Jominy testing, static tensile testing, an optical microscope (OM), scanning electron microscopy (SEM) and double cantilever beam (DCB) testing. The results show that the addition of 0.015% Ti and 0.002% B into a medium-carbon Fe-Cr-Mo-Nb-V steel increased the hardenability and refined the PAGS and quenched martensite packets, and the size of carbides was reduced. It is believed that these behaviors are responsible for the improvement in the threshold stress intensity factor K_ISSC.