Friction stir welding (FSW) is an alternative method to join aluminum (Al) alloys in a solid-state condition. However, the coarsening or dissolution of precipitation hardening phases in the welding zone causes strength reduction or softening behavior in the welded area of age-hardened Al alloys. Therefore, this research aimed to improve the mechanical properties of an FSW Al–Mg–Si alloy via post-weld heat treatment (PWHT) and the possibility of controlling the abnormal grain growth (AGG) using different welding parameters. FSW was performed with different rotational and travel speeds, and T6 heat treatment was carried out on the FSW samples as the PWHT. The results showed a decrease in the strength of the FSW samples compared with that of the base material (BM) due to the dissolution of precipitation hardening particles in the heat-affected zone. However, the emergence of AGG in the microstructure after the T6-PWHT was identified as the potential event in the microstructure of the PWHT samples. It is found that the AGG of the microstructure in similar joints of Al6061(T6) was governed by the welding parameters. The results proved that PWHT was able to increase the tensile properties of the welded samples to values comparable to that of Al6061(T6)-BM. The increased mechanical properties of the FSW joints were attributed to a proper PWHT that resulted in a homogeneous distribution of the precipitation hardening phases in the welding zones.

In this study, the effect of phase, microstructure, and porosity in Selective Laser Melting (SLM) on hardness, tensile, and fracture behavior of 17-4 PH was investigated. The increasing interest in SLM in producing complex parts has encouraged the industry to produce performance parts, such as martensitic 17-4 PH stainless steel. However, the microstructure and mechanical behavior of SLM 17-4PH is not fully understood by researchers. Understanding the microstructure profile is complex because it is driven by thermal history and porosity. Both elements vary, based on the build directions, further hindering researchers from fully understanding the mechanical properties. To fabricate specimens in three different building orientations (0°, 45°, and 90°), 17-4 powder was used. Two phases, namely, austenite and martensite, with 90° build direction, retained more austenite, due to the reheating process on a smaller base area. The optical microstructure revealed several elements that were distinct for SLM processing, including circular, columnar lath, wave melt pool, and porosity. Columnar lath was found to grow continuously across different melt pools. Hardness was found to be higher for 0° than for 90°, due to higher martensite content. Tensile strength was highest for 0°, at 958 MPa, higher than at 45° and 90° at 743 and 614 MPa, respectively. Porosity analysis validated that 90° had all three types of porosities and, specifically, the crescent type, which held un-melted powders. All types of porosities were found in fractography analysis.

The 5083 and 6061(T6) aluminum (Al) alloys are widely used in transportation industries and the development of structural designs because of their high toughness and high corrosion resistance. Friction stir welding (FSW) was performed to produce the dissimilar welded joint of Al5083-Al 6061(T6) under different welding parameters. However, softening behavior occurred in the friction stir welded (FSWed) samples because of grain coarsening or the dissolution of precipitation-hardening phases in the welding zone. Consequently, this research intended to investigate the effect of the post-weld heat treatment (PWHT) method on the mechanical property improvement of the dissimilar FSWed Al5083-Al6061(T6) and governing abnormal grain growth (AGG) through different welding parameters. The results showed PWHT enhanced the mechanical properties of dissimilar joints of Al5083-Al6061(T6). AGG was obtained in the microstructure of PWHTed joints, but appropriate PWHT could recover the dissolved precipitation-hardening particle in the heat-affected zone of the as-welded joint. Further, the tensile strength of the dissimilar joint increased from 181 MPa in the as-welded joint to 270 MPa in the PWHTed joint, showing 93% welding efficacy.

5083 aluminium (Al) alloy materials have extensive structural applications in transportation industries because of their high strength-to-weight ratio and corrosion resistance. However, under conventional fusion weldings, these materials are limited by their porosity, hot cracking, and distortion. Herein, friction stir welding (FSW) was performed to join a similar AA5083 alloy. A post-weld cold-rolling (PWCR) process was applied on joint samples at different thickness-reduction percentages (i.e., 10%, 20%, and 40%) to identify the effect of strain hardening on the microstructure and mechanical properties of the friction-stir-welded joint of AA5083 while considering the serration-flow behaviour at stress–strain curves and dislocation density of the post-weld cold-rolled (PWCRed) samples. FSW induced a 20% reduction in the tensile strength of the joint samples relative to the base metal. PWCR also reduced the average grain size at the nugget zone and base metal because of the increase in plastic deformation imposed on the samples. Furthermore, PWCR increased the dislocation density because of the interaction among dislocation stress fields. Consequently, the tensile strength of the friction-stir-welded joint increased with the increased cold-rolling percentage and peaked at 403 MPa for PWCRed–40%, which significantly improved the serration-flow behaviour of stress–strain and welding efficiency up to 123%.