This is a study on how to reduce shrinkage and improve crack resistance of foamed concrete. By selecting different curing temperatures and humidity, six different curing conditions were analyzed. The shrinkage deformation and maximum crack width of foamed concrete blocks with water–cement ratios of 0.4 and 0.5, under six curing conditions, were measured by a comparator and optical microscope, and the cracking time was recorded. The effects of curing temperature, humidity and water–cement ratio on the shrinkage and crack resistance of the foamed concrete were analyzed by comparing the experimental results of each group. We studied the primary and secondary order of the three factors affecting the drying shrinkage of foamed concrete. The results show that: temperature is the primary factor that changes the drying shrinkage performance of foamed concrete, followed by the water–cement ratio, and finally humidity. The interaction of these three factors is not obvious. The shrinkage of foamed concrete increases with the increase in temperature; increasing the humidity of curing can control the water loss rate of foamed concrete and reduce shrinkage. Lower humidity and higher temperature will make cracks appear earlier; with an increase in the water–cement ratio, the initial cracking time is shortened and the cracking property of foamed concrete is improved.

Hydromechanical and structural properties of compacted loess have a significant impact on the stability and reliability of subbase and subgrade, which needs to be quickly determined in the field and laboratory. Hence, an electrical resistivity method was used to characterize the hydromechanical and structural properties of compacted loess during constant rate of strain compression. In the present work, compacted loess samples with a dry density of 1.7 g/cm³, a diameter of 64 mm, a height of 10 mm and different water content ranging from 5–25% were prepared. The constant rate of strain (CRS) tests were conducted by a developed oedometer cell equipped with a pair of horizontal circular electrodes (diameter of 20 mm) and vertical rectangular electrodes (width of 3.5 mm) to determine the electrical resistivity of compacted loess. The results showed that as average water content increases, plastic compression indices increase from 0.220 to 0.350 and the elastic compression indices increase from 0.0152 to 0.030, but they decrease to 0.167 and 0.010 and yield stress decreases from 381.28 kPa to 72.35 kPa. Moreover, as vertical strain increases, the variation trend of average formation factor and average shape factor for the lower water content decreases but increases for the maximum water content, and the anisotropy index first decrease and then tend to increase slightly, which indicates that the structural properties of unsaturated and saturated samples during compression exhibits different trend and the anisotropy of samples tend to be stable as vertical strain increases. As the water content increases, the average formation factor and average shape factor decrease, but the anisotropy index first decreases then increases, suggesting that water content has a significant impact on these electrical indices. More important, The coefficients of average formation factor decrease from 33.830 to −1.698 and the coefficients of average shape factor decrease from 8.339 to −0.398 as water content increases, whereas there is less variation for the coefficient of anisotropic index with a value of 2.190. An equation correlating average formation factor and water content and vertical strain is regressed to characterize the hydromechanical properties of compacted loess by measuring its impedance, which can be used to evaluate the stability of compacted loessic ground and subgrade.

Because of the strong alkalinity of red mud, it is difficult to recycle, and the long-term accumulation of red mud causes environmental pollution. The study shows that the solidification characteristics of bayer red mud (RM) under the action of Ca(OH)₂ (CH) are obvious. The mechanical properties of Bayer RM paste with different amounts of CH at different ages were tested. The strength of RMCH gradually increases with the increase in CH content and age, reaching a turning point in strength at 26.4% content of CH, with the highest strength at 28 days, reaching 2.73 MPa. The solidification products were characterized by XRD, FTIR, TG-DTG, and SEM-EDS. The results show that under the action of CH, the main solidification products of RM are C-(A)-S-H, hemicarboaluminate, and monocarboaluminate. In the solidification process, hydroxysodalite and faujasite-Na react with CH to generate C-S-H, Al(OH)₄⁻, and Na⁺, then react to generate hemicarboaluminate, monocarboaluminate and C-(A)-S-H, among which hemicarboaluminate is transformed into monocarboaluminate in the presence of calcite, and further monocarboaluminate decomposes to generate calcite. It provides a basis for the study of the interaction mechanism between a single substance and RM and provides a research basis for the sustainable utilization of red mud.

Foamed concrete is mostly used for backfilling of long-distance tunnels and compressive strength is an important technical index to control the quality of foamed concrete. The influence factors on compressive strength of low-density foamed concrete were obtained by the single factor test method based on the targeted dry density and compressive strength. The results show that the HT composed of pollution-free animal protein oil and vegetable oil is an efficient foaming agent and can produce stable foams. The cementation ability of cement can be fully expressed when a water to cement ratio of 0.45~0.5 is employed, making foamed concrete have a compressive strength higher than 2 MPa. The foam content is inversely proportional to the compressive strength and dry density of foamed concrete, and the volume ratio of slurry to foam should be 2:1~3:1. The content of fly ash is also inversely proportional to the compressive strength but positively proportional to the dry density. When the content of admixture is 40~55%, the compressive strength of foamed concrete with low density is not less than 2 MPa. The mixing proportion can be changed in the reasonable range to meet the requirements of different projects.

In engineering practice, unsaturated compacted loess is often utilized as a filling material in the loess regions. The loess inevitably undergoes one-dimensional compressibility and creep deformation due to the long-term effects of the upper soil layers and buildings. When the deformation is large enough, it tends to damage buildings and threaten engineering safety. In this regard, the one-dimensional compressibility and creep properties of unsaturated compacted loess based on incremental loading (IL) and constant rate of strain (CRS) methods have been studied. First, soil materials with an initial moisture content of 15% were prepared and then compacted into soil samples with an 80 mm diameter and a 10 mm height. Second, the compressibility and creep properties of the compacted loess samples obtained via the IL and CRS compression tests were compared and analyzed. In this study, several parameters, including the primary compression index C_c and secondary compression index C_α, were derived. Meanwhile, the moisture content of the samples was measured via electrical resistivity methods. Finally, the microstructural characteristics were derived via nuclear magnetic resonance (NMR) and scanning electron microscopy (SEM) tests. The results showed that C_c and C_α increased with the increase in moisture content and vertical stress; C_α/C_c ranged from 0.026 to 0.042. Compared with the compression parameters and deformation of the samples, those obtained via the CRS tests are a little larger than those obtained via the IL tests for a given loading and initial moisture content. The electrical resistivity depends on pore water-connected channels, which were deeply affected by the initial moisture content, vertical stress and loading duration (or strain rate). Moreover, as vertical stress increased, the pore size and pore area gradually decreased, the coarse particles were broken, and the fine particles increased. The contacts between particles changed from point-to-point contacts and edge-to-edge contacts to face-to-face contacts. Meanwhile, as vertical stress and loading rate increased, the loess particles were apt to vary from irregular elongated particles to equiaxial circular particles. This investigation can provide a theoretical base and experimental support for improving ground stability and preventing landslide disasters in loess regions.