Polylactic acid (PLA) and polyglycolic acid (PGA) are well-known medical-implant materials. Under the consideration of the limitations of degradable polymeric materials, such as weak mechanical strength and by-product release through the biodegradation process under in vivo environments, PLA–PGA block copolymer is one of the effective alternative implant materials in the clinical field. In our previous study, two types of extremely effective PGA–PLA copolymers (multi/tri-block PGA–PLA copolymers) were synthesized. These synthesized block copolymers could overcome aforementioned issues and also showed good biocompatibility. In this study, the PGA–PLA block copolymers with large molecular weight were synthesized under the same chemical scheme, and their bio durability was confirmed through the in vivo degradation behavior and histochemical analyses (by hematoxylin and eosin and immune staining) in comparison with commercial PLGA random copolymer (medical grade). Specimens for the degradation test were investigated by SEM and X-ray diffractometer (XRD). As a result, the synthesized PGA–PLA block copolymer showed good biocompatibility and had a controlled biodegrading rate, making it suitable for use in resorbable spinal-fixation materials.

We synthesized and evaluated biodegradable and elastomeric polyesters (poly(glycerol sebacate) (PGS)) using polycondensation between glycerol and sebacic acid to form a cross-linked network structure without using exogenous catalysts. Synthesized materials possess good mechanical properties, elasticity, and surface erosion biodegradation behavior. The tensile strength of the PGS was as high as 0.28 ± 0.004 MPa, and Young's modulus was 0.122 ± 0.0003 MPa. Elongation was as high as 237.8 ± 0.64%, and repeated elongation behavior was also observed to at least three times the original length without rupture. The water-in-air contact angles of the PGS surfaces were about 60°. We also analyzed the properties of an electrospray coating of biodegradable PGS on a nitinol stent for the purpose of enhancing long-term patency for the therapeutic treatment of varicose veins disease. The surface morphology and thickness of coating layer could be controlled by adjusting the electrospraying conditions and solution parameters.