The dyeing and finishing step represents a clear hotspot in the textile supply chain as the wet processing stages require significant amounts of water, energy, and chemicals. In order to tackle environmental issues, natural dyes are gaining attention from researchers as more sustainable alternatives to synthetic ones. This review discusses the topic of natural dyes, providing a description of their main features and differences compared to synthetic dyes, and encompasses a summary of recent research in the field of natural dyes with specific reference to the following areas of sustainable innovation: extraction techniques, the preparation of substrates, the mordanting process, and the dyeing process. The literature review showed that promising new technologies and techniques have been successfully employed to improve the performance and sustainability of natural dyeing processes, but several limitations such as the poor fastness properties of natural dyes, their low affinity with textiles substrates, difficulties in the reproducibility of shades, as well as other factors such as cost-effectiveness considerations, still prevent industry from adopting natural dyes on a larger scale and will require further research in order to expand their use beyond niche applications.

The objective of this work was to assess the possibility of dyeing a substrate composed of non-textile industrial hemp using natural dyes from common madder (Rubia Tinctorum L.) and calendula (Calendula Officialis) and tannin and alum as mordants. The substrate used for the dyeing had a 25/75 hemp/cotton composition. The hemp raw material is an agricultural by-product that was subjected to mechanical and chemical treatments in order to cottonize the fibers, blend them with cotton, and thus obtain first 40-tex open-end yarns and then a knitted fabric. The latter was subjected to different dyeing conditions by varying the dye, mordant, and method for its application, type of water, and rinsing after dyeing. Measurements of the difference (ΔE) and intensity (K/S) of color and fastness to washing and rubbing were carried out. The results showed that dyeing of a non-textile residual hemp substrate is possible, and that calendula is a good option for dyeing it with tap water, tannin-alum set in a meta-mordanting process, and rinsing after 24 h. In this way, a contribution has been made to the circular economy of the textile industry through the use of more sustainable sources and products.

Nanocomposite carbon-paste electrodes (NC-CPEs) have been investigated for the first time in electrolyte-gated organic field-effect transistors (EGOFETs) as a replacement of conventional metal gate electrodes, using carbon nanotubes (CNTs) as a model carbon filler. Interestingly, the electrical properties of the resulting devices have been modulated by changing the loading percentage of CNTs within the insulating polymeric matrix. The potential of using such non-conventional gate electrodes for sensing purposes has also been evaluated by investigating, as a proof of concept, the formation of a supramolecular complex between a functionalized CNT-based NC-CPE containing β-cyclodextrin (β-CD) as a bio-recognition element and tryptophan (TRP). This approach, in synergism with the amplification function of an EGOFET, affords a shift in the threshold voltage (V_TH) of the transistor, giving promising analytical results with detection limits at picomolar levels (1.0 ± 0.1 pM) as well as a linear response from 10⁻¹² to 10⁻⁹ M. Accordingly, NC-CPEs have been demonstrated to be a potential alternative to metal gate electrodes for the development of a new generation of highly sensitive carbon-based EGOFET bio-sensors.

The inclusion of particles in a polymeric substrate to achieve certain properties is a well-known practice. In the case of textile substrates, this practice may deeply affect the structure of the produced yarns, as even a filament with no textile applications can be obtained. In this manuscript, titanium dioxide (TiO₂) particles were incorporated into polyester (PET) chips and the influence of these fillers on the properties of yarn and fabric, and the ultraviolet protection factor (UPF) was assessed. For this purpose, rutile and anatase crystalline forms of TiO₂, as well as the size of the particles, were evaluated. Moreover, parameters such as mechanical properties, orientation of the macromolecules and thermal behavior were analyzed to ensure that the textile grade is maintained throughout the production process. The results showed that the inclusion of micro- and nanoparticles of TiO₂ decreases the molecular weight and tenacity of PET. Also, although orientation and crystallinity varied during the textile process, the resulting heatset fabrics did not present important differences in those parameters. Finally, the attainment of textile-grade PET-TiO₂ fabrics with UPF indexes of 50+ with both rutile and anatase and micro- and nano-sized TiO₂ forms was demonstrated.

Two different types of calcium fluoride (CaF₂) particles were incorporated into a poly(ethylene terephthalate) (PET) matrix, fine particles (∼350 nm), and nanoparticles (∼70 nm). Both of them were synthesized by a chemical precipitation method using triethanolamine (TEA) as stabilizer. To obtain the nanoparticles, a greater amount of TEA was added during the synthesis in order to limit their growth. Therefore, unlike the fine particles, nanoparticles contained a greater amount of the stabilizer. Once CaF₂ particles were obtained, the composite materials were prepared by melt-blending PET and particles at different filler loadings. The influence of both kinds of particles on the non-isothermal crystallization behavior of PET was investigated by using differential scanning calorimetry and field emission scanning electron microscopy. The Jeziorny-modified Avrami equation was applied to describe the kinetics of the non-isothermal crystallization, and several parameters were analyzed (half-crystallization time, Avrami exponent, and rate constant). According to the results, it is clear that CaF₂ particles act as nucleating agents, accelerating the crystallization rate of PET. However, the effect on the crystallization rate was more noticeable with the addition of the fine particles where the surface plays an important role for epitaxial crystallization, while the addition of the nanoparticles with an organic surface coating resulted in a crystallization behavior similar to the observed for PET.