Background: This study investigated the remineralisation effect of bioactive glass on artificial dentine caries. Methods: Dentine disks with artificial caries were treated with bioactive glass (group BAG), casein phosphopeptide–amorphous calcium phosphate (CPP-ACP) (group CPP-ACP), sodium fluoride glycerol (group F) or deionized water (group W). All disks were subjected to pH cycling for 28 days subsequently. The topography, microhardness and remineralisation depth of the dentine carious lesion were assessed by atomic force microscopy (AFM), microhardness testing and confocal laser scanning microscope (CLSM), respectively. Results: AFM images indicated mineral depositions on the surface of the carious lesion in group BAG. The changes of Vickers hardness number (ΔVHN, mean ± SD) after pH cycling were 9.67 ± 3.60, 6.06 ± 3.83, 5.00 ± 2.19 and − 1.90 ± 2.09 (p < 0.001) in group BAG, group CPP-ACP, group F and group W, respectively. The remineralisation depth (mean ± SD) of the carious lesion in group BAG, group CPP-ACP, group F and group W were 165 ± 11 μm, 111 ± 11 μm, 75 ± 6 μm and 0 μm (p < 0.001), respectively. Conclusion: Bioactive glass possessed a promising remineralisation effect on artificial dentine caries and could be a therapeutic choice for caries management.

We recruited 1296 mothers in their first trimester from the Affiliated Obstetrics and Gynecology Hospital of Nanjing Medical University between May 2014 and September 2015 to investigate the associations of maternal, perinatal and postnatal factors with the eruption timing of the first primary tooth (ETFPT) in a Chinese population. We collected maternal demographic information and clinical data during the perinatal and postnatal period, and oral examinations of the infants were performed by a doctor at 6, 9 and 12 months of age. Multiple regression analysis was used to identify significant explanatory variables for ETFPT. The mean age at eruption of the first primary tooth for all the infants was 6.82 ± 1.90 months. After adjustment for confounders, higher maternal childbearing age (β = 0.57; 95%CI = 0.13–1.02), female sex (β = 0.26; 95%CI = 0.07–0.52), and low birth weight (β = 0.98; 95%CI = 0.20–1.76) were significantly associated with delayed eruption of the first primary tooth, while macrosomia (β = −0.79; 95%CI = −1.30–−0.28) was significantly associated with earlier eruption of the first primary tooth. Maternal childbearing age, infant sex and infant birth weight were significant determinants of ETFPT.

To establish a three-dimensional (3D) finite element (FE) model of a maxillary first premolar and to evaluate the stress generated on the tooth (dentine) and on the indirect composite resin restorations by occlusal forces. An embedded intact maxillary first premolar tooth was sliced serially and scanned digitally parallel to the occlusal surface. The 64 images were assembled in a 3D FE mesh and exported to generate a 3D solid tooth model. Simulated, adhesively cemented indirect mesial-occlusal-distal (MOD) inlays of 2 mm (I1), 3 mm (I2) and 4 mm (I3) in width, and MOD onlays with occlusal cusp coverage of 2 mm (O1) and 3 mm (O2) in depth were created. The peak von Mises stress values in the five tooth models resulting from static vertical and oblique occlusal forces (300 N) were evaluated using Patran FE software. The peak stress values generated by vertical occlusal force generated in dentine of I1, I2, I3, O1 and O2 restoration were 67, 32, 29, 38 and 27 MPa, respectively, and those generated by oblique occlusal force were 52, 114, 168, 54 and 55 MPa, respectively. The peak von Mises stress values in I1, I2, I3, O1 and O2 restoration subjected to oblique occlusal loading were 79, 120, 1740, 1400 and 1170 MPa, respectively. A 3D FE model of a maxillary first premolar was established. Simulated cemented composite resin onlay markedly reduces occlusal stress in the underlying dentine of large MOD preparation. Oblique occlusal force imparts substantially higher stress to large composite resin inlay than to the adjacent dentine.

The current study aims to investigate a suitable adhesive for primary tooth enamel. Shear bond strength (SBS) of primary teeth and the length of resin protrusion were analyzed using one-way ANOVA with Bonferroni multiple comparison tests after etching with 35% H3PO4. SBS and marginal microleakage tests were conducted with Single Bond Universal (SBU)/Single Bond 2 (SB2) adhesives with or without pre-etching using a nonparametric Kruskal-Wallis test. Clinical investigations were performed to validate the adhesive for primary teeth restoration using Chi-square tests. Results showed that the SBS and length of resin protrusion increased significantly with the etching time. Teeth in the SBU with 35% H3PO4 pre-etching groups had higher bond strength and lower marginal microleakage than those in the SB2 groups. Mixed fractures were more common in the 35% H3PO4 etched 30 s + SB2/SBU groups. Clinical investigations showed significant differences between the two groups in cumulative retention rates at the 6-, 12-and 18-month follow-up evaluations, as well as in marginal adaptation, discoloration, and secondary caries at the 12-and 18-month follow-up assessments. Together, pre-etching primary teeth enamel for 30 s before SBU treatment improved clinical composite resin restoration, which can provide a suitable approach for restoration of primary teeth.