We demonstrate that some assemblies of anisometric nanoparticles could be the ideal agents to optimize the response to external AC fields for magnetic fluid hyperthermia in viscous environments.

Uniform size cobalt ferrite nanoparticles have been synthesized in one step using an electrochemical technique. Synthesis parameters such as the current density, temperature and stirring were optimized to produce pure cobalt ferrite. The nanoparticles have been investigated by means of magnetic measurements, Mössbauer spectroscopy, x-ray powder diffraction and transmission electron microscopy. The average size of the electrosynthesized samples was controlled by the synthesis parameters and this showed a rather narrow size distribution. The x-ray analysis shows that the CoFe(2)O(4) obtained presents a totally inverse spinel structure. The magnetic properties of the stoichiometric nanoparticles show ferromagnetic behavior at room temperature with a coercivity up to 6386 Oe and a saturation magnetization of 85 emu g(-1).

A series of zinc ferrite nanoparticles were synthesized following a single-step electrochemical method in aqueous medium. This strategy allowed the control of both the size and chemical composition of the nanoparticles in an easy and reproducible manner by simply varying the intensity of the applied current. The obtained nanoparticles were morphologically and structurally characterized as a function of the particle size and the Zn content in the sample by X-ray diffraction (XRD), transmission electron microscopy (TEM), inductively coupled plasma emission spectroscopy (ICP) and Raman microscopy. The formation of Zn_xFe_(3−x)O₄ (x = 0.18–0.93) ferrite nanoparticles with crystal sizes in the range of 9 to 18 nm and with a homogeneous distribution of the Zn²⁺ cation in the crystalline structure was observed. However, following a thermal treatment, a migration of zinc cations was detected that led to the formation of two different crystalline phases, stoichiometric zinc ferrite and hematite. Raman microscopy revealed the formation of segregated micro-domains enriched within these crystalline phases. The study of the magnetic properties of the electro-synthesized ferrite nanoparticles with a homogeneous incorporation of Zn in the structure shows that the saturation magnetization and the coercively values are highly dependent on the chemical composition and crystal size.