We have successfully developed novel surface-enhanced Raman scattering (SERS) substrates with three-dimensional (3D) porous structures for effectively improving the sensitivity and reproducibility of SERS, which can rapidly detect small molecules (rhodamine 6G as an example). Periodical arrays of the honeycomb-like substrates were fabricated by self-assembling polyurethane-co-azetidine-2,4-dione (PU-PAZ) polymers. PU-PAZ comprising amphiphilic dendrons could stabilize the phase separation between the water droplets and polymer solution, and then organize into regular porous structures during the breath figure method. Subsequently, SERS substrates were fabricated by immobilizing gold nanoparticles (AuNPs) onto the honeycomb-like films with various 3D porous structures, controlled by the different PU-PAZ concentrations and relative humidities. Results show that surface enhancement factors of honeycomb-like substrates were 20 times higher than that of flat-film substrates (control group) due to enormous hot-spots resonance effects by the 3D porous structure, verified through Raman mapping at various positions of the z-axis. Furthermore, the particle size effects were evaluated by immobilized 12 and 67 nm of AuNPs on the honeycomb-like substrates, indicating larger AuNPs could induce more pronounced hot-spots effects. The generation of hot-spots resonance to enhance Raman intensity is strongly dependent on the diameter of AuNPs and the pore size of the honeycomb-like and 3D porous substrates for label-free and rapid SERS detection.

In this study, a novel hemocompatible coating on stainless steel substrates was prepared by electrochemically copolymerizing 3,4-ethylenedioxythiophene (EDOT) with graphene oxide (GO), polystyrene sulfonate (PSS), or heparin (HEP) on SUS316L stainless steel, producing an anti-fouling (anti-protein adsorption and anti-platelet adhesion) surface to avoid the restenosis of blood vessels. The negative charges of GO, PSS, and HEP repel negatively charged proteins and platelets to achieve anti-fouling and anti-clotting. The results show that the anti-fouling capability of the poly(3,4-ethylenedioxythiophene) (PEDOT)/PSS coating is similar to that of the PEDOT/HEP coating. The anti-fouling capability of PEDOT/GO is higher than those of PEDOT/HEP and PEDOT/PSS. The reason for this is that GO exhibits negatively charged functional groups (COO⁻). The highest anti-fouling capability was found with the PEDOT/GO/HEP coating, indicating that electrochemical copolymerization of PEDOT with GO and HEP enhances the anti-fouling capability. Furthermore, the biocompatibility of the PEDOT coatings was tested with 3T3 cells for 1–5 days. The results show that all PEDOT composite coatings exhibited biocompatibility. The blood clotting time (APTT) of PEDOT/GO/HEP was prolonged to 225 s, much longer than the 40 s of pristine SUS316L stainless steel (the control), thus greatly improving the anti-blood-clotting capability of cardiovascular stents.