This study measured and analyzed the mechanical properties of normal aggregate concrete (NC) and lightweight aggregate concrete (LC) subjected to high temperatures. The target temperature was set to 100, 200, 300, 500, and 700 °C, and W/C was set to 0.41, 0.33 and 0.28 to evaluate high temperature properties at various intensities. Measurement parameters included mass loss, compressive strength, ultrasonic pulse velocity (UPV), and elastic modulus. We compared the residual mechanical properties between the target and preheating temperatures (20 °C) and then analyzed the correlation between UPV and compressive strength. According to the research findings, after exposure to high temperatures, LC demonstrated a higher mass reduction rate than NC at all levels and exhibited higher residual mechanical properties. The results of analyzing the correlation between compressive strength and UPV for concrete subjected high temperatures were very different from the compressive strength prediction equation previous proposed at room temperature, and the error range of the residual strength prediction equation considering W/C was reduced.

The effects or high CaO fly ash and sulfate activator on cementless grouting material were investigated through Labiles Waterglass (LW) grouting applied at an actual construction field. Circulating fluidized bed combustion ash was used as CaO fly ash, and petro cokes desulfurization gypsum was used as sulfate activator. Cementless grouting material (CGM) could decrease the gel time by about 16.7% compared with ordinary Portland cement (OPC). This characteristic improved the average daily workload and construction period per meter by about 13.5% with CGM. Furthermore, when constructing 1000 holes of LW grouting, the construction time could be reduced by 19 days (20% of the total construction period of LW grouting). Meanwhile, CGM could increase the homogel strength by about 48.4% after 28 days compared with OPC. After X-ray diffraction analysis and scanning electron microscope analysis, CGM was found to produce cement hydrate by chemical reaction mechanism of high CaO fly ash and sulfate activator, even though cement was not used. The matrix structure properties of CGM and OPC specimens were similar, but CGM, with 134.3% fineness, exhibited higher compressive strength and lower air permeability than OPC. As a result, CGM could reduce the leakage length per square meter by 74.4% compared with OPC. Using CGM as a substitute for OPC in LW grouting in actual sites could be beneficial in terms of securing construction speed and durability, as well as reducing CO₂ emissions due to reduction of OPC usage.

In this study, experiments were performed on the applicability of mortars and concretes based on calcium sulfoaluminate (CSA) binders to facilitate the early strength development of ordinary Portland cement (OPC) under low-temperature conditions. An optimum mixture of CSA was evaluated to improve the early strength of OPC, and the effects of accelerators and retarders on this mixture were examined to demonstrate the applicability of the resulting concrete mixture. Furthermore, mixture applicability was validated by producing concrete at the Remicon Batcher plant and performing numerical simulations. As observed, the optimum CSA substitution rate for the realization of early strength was 17% of the total unit binder amount with CaO/SO₃ and SO₃/Al₂O₃ ratios of 1.9 and 1.25, respectively. Evidently, CSA in combination with Na₂SO₄ as an accelerator promoted the early strength of concrete with OPC and secured its constructability using additional retarders to control the quick setting of concrete. Additionally, the activation of initial hydration at low temperatures yielded a compressive strength of 5 MPa/12 h or higher for the resulting concrete mixture.

In this study, the influences of chemical composition and fineness on the development of concrete strength by curing conditions were investigated through performance evaluation of high SO₃ Portland cement (HSPC) and ordinary Portland cement (OPC). At the same fineness (3800 cm²/g), the initial and final setting times of HSPC were 92 and 98 min less than OPC. Early mortar compressive strength was approximately 176% higher after 24 h. After curing for 15 h, 18 h, and 24 h, the maturity of HSPC concrete (107.4%, 109.6%, and 111.7%) and early compressive strength (146.4%, 170.7%, and 154.5%) were higher than measured for OPC concrete. HSPC fineness was 111.8% higher than OPC, leading to early activation of the hydration reaction. By X-ray fluorescence analysis, the SO₃ content of HSPC was 107.9% that of OPC. The applicable time for HSPC concrete form removal was shorter than that for OPC concrete. The relationships y = −10.57 ln(x) + 47.30 and y = −9.84 ln(x) + 44.05 were estimated for predicting the early-age strength OPC and HSPC concrete. Therefore, applying HSPC concrete to an actual construction site is expected to shorten the construction period and reduce the heating curing cost in winter compared to OPC concrete.

This study aimed to evaluate the durability and engineering performance of concrete mixed with locally produced ground granulated blast-furnace slag (GGBS) based on CaO content and ratio, and to derive the optimal CaO content range that can secure durability. Hence, tests were conducted by increasing the GGBS replacement ratio by 10% from 0% to 70%, while the unit binder weight was fixed at 330 kg/m³. The results indicated that the compressive strength exhibited a tendency to increase when the CaO content and basicity increased within 28 d of age, although similar compressive strength characteristics were observed at 56 d of age, irrespective of the CaO content and basicity. Additionally, four test items (i.e., carbonation depth, chloride penetration depth, relative dynamic elastic modulus, and weight reducing ratio) were measured to evaluate durability. The optimal CaO content satisfying all four parameters was observed as ranging between 53% and 56% (GGBS replacement ratio: 27.5%–47.1%). The results of the study can provide guidelines on the mixing proportions of GGBS concrete with excellent durability that can be applied to local construction sites and can be used as basic data to set chemical composition criteria for the development of binders to improve durability.

This study classified the strength of normal aggregate concrete (NC) and lightweight aggregate concrete (LC) into three levels (30, 45, and 60 MPa). In particular, the compressive strength, ultrasonic pulse velocity, and elastic modulus were measured and analyzed at the ages of 1, 3, 7, and 28 days to establish the correlation between the compressive strength and the ultrasonic pulse velocity and between the elastic modulus and the ultrasonic pulse velocity. In addition, this study proposed strength and elastic modulus prediction equations as functions of the ultrasonic pulse velocity. The developed equations were compared with previously proposed strength prediction equations. The results showed that the measured mechanical properties of NC tended to be higher at all ages than in LC. However, LC45 exhibited relatively high compressive strength compared to NC45. The relative mechanical properties of LC compared to NC were the highest at 45 MPa and the lowest at 60 MPa. The relative ultrasonic pulse velocity converged at all levels as the age increased. Moreover, the correlation between the compressive strength and the ultrasonic pulse velocity in LC exceeded that of NC, and in LC, the correlation coefficient decreased as the strength increased. The correlation coefficients between the elastic modulus and the ultrasonic pulse velocity were high at all levels except for LC45. Finally, this study proposed compressive strength and elastic modulus prediction equations as an exponential function of LC. The proposed equations outperformed the previously proposed strength prediction equations.