Surface-enhanced Raman spectroscopy (SERS) applications in clinical diagnosis and spectral pathology are increasing due to the potential of the technique to bio-barcode incipient and differential diseases via real-time monitoring of biomarkers in fluids and in real-time via biomolecular fingerprinting. Additionally, the rapid advancements in micro/nanotechnology have a visible influence in all aspects of science and life. The miniaturization and enhanced properties of materials at the micro/nanoscale transcended the confines of the laboratory and are revolutionizing domains such as electronics, optics, medicine, and environmental science. The societal and technological impact of SERS biosensing by using semiconductor-based nanostructured smart substrates will be huge once minor technical pitfalls are solved. Herein, challenges in clinical routine testing are addressed in order to understand the context of how SERS can perform in real, in vivo sampling and bioassays for early neurodegenerative disease (ND) diagnosis. The main interest in translating SERS into clinical practice is reinforced by the practical advantages: portability of the designed setups, versatility in using nanomaterials of various matter and costs, readiness, and reliability. As we will present in this review, in the frame of technology readiness levels (TRL), the current maturity reached by semiconductor-based SERS biosensors, in particular that of zinc oxide (ZnO)-based hybrid SERS substrates, is situated at the development level TRL 6 (out of 9 levels). Three-dimensional, multilayered SERS substrates that provide additional plasmonic hot spots in the z-axis are of key importance in designing highly performant SERS biosensors for the detection of ND biomarkers.

The increasing pollution of surface and groundwater bodies by pharmaceuticals is a general environmental problem requiring routine monitoring. Conventional analytical techniques used to quantify traces of pharmaceuticals are relatively expensive and generally demand long analysis times, associated with difficulties in performing field analyses. Propranolol, a widely used β-blocker, is representative of an emerging class of pharmaceutical pollutants with a noticeable presence in the aquatic environment. In this context, we focused on developing an innovative, highly accessible analytical platform based on self-assembled metal colloidal nanoparticle films for the fast and sensitive detection of propranolol based on Surface Enhanced Raman Spectroscopy (SERS). The ideal nature of the metal used as the active SERS substrate was investigated by comparing silver and gold self-assembled colloidal nanoparticle films, and the improved enhancement observed on the gold substrate was discussed and supported by Density Functional Theory calculations, optical spectra analyses, and Finite-Difference Time-Domain simulations. Next, direct detection of propranolol at low concentrations was demonstrated, reaching the ppb regime. Finally, we showed that the self-assembled gold nanoparticle films could be successfully used as working electrodes in electrochemical-SERS analyses, opening the possibility of implementing them in a wide array of analytical applications and fundamental studies. This study reports for the first time a direct comparison between gold and silver nanoparticle films and, thus, contributes to a more rational design of nanoparticle-based SERS substrates for sensing applications.

Plasmonic noble metal nanostructured films have a huge potential for the development of efficient, tunable, miniaturized optical sensors. Herein, we report on the fabrication and characterization of gold-coated nanopost arrays, their use as refractometric sensors, and their optimization through photonics simulations. Monolithic square nanopost arrays having different period and nanopost size are fabricated by nanoimprint lithography on polymer foils, and sputter-coated by gold films. The reflectivity of these gold nanopost-shell arrays present dips in the visible range, which are efficient for refractometric sensing. By finite-difference time-domain (FDTD) simulations we reproduce the experimental spectra, describe the electric fields distribution around the nanopost-shells, and then explain their good sensitivity, around 450 nm/RIU. Furthermore, we determine by simulations the influence of several geometrical parameters, such as array period, nanopost width, gold film thickness, and nanopost side coverage on both reflectivity spectra and sensing capabilities. Fully coated nanoposts provide an extremely deep reflectivity minimum, approaching zero, which makes the relative reflectivity change extremely high, more than two orders of magnitude higher than for partially coated nanoposts. These results contribute to the understanding of the plasmonic properties of metal coated nanopost arrays, and to the development of efficient platforms for sensing and other surface plasmon based applications.

The combination of layered double hydroxides (LDH) with graphene oxide (GO) enables the formation of nanohybrids with improved properties. This work focuses on the structural and catalytic properties of Ce-containing MgAl LDH-GO composites bearing different concentrations of GO in the range of 5–25 wt.%. The synthesis of the composites was performed by co-precipitating the LDH phase in the presence of GO, while their characterization was performed using XRF, XRD, DRIFT, Raman, SEM, nitrogen adsorption-desorption, and acidity-basicity measurements. The LDH-GO composites, showing redox, basic, and acid catalytic functions, were tested in two different types of organic transformations: (i) Knoevenagel condensation and (ii) one-pot cascade oxidation-Knoevenagel condensation. (i) The cinnamic acid was synthesized by the Knoevenagel condensation of benzaldehyde with diethylmalonate. The composites showed catalytic performances in strong contrast to neat LDH or GO, suggesting a synergistic interaction between the two components. During Knoevenagel condensation, the catalytic activity increased with the GO content in the hybrids up to 15 wt.% and decreased afterwards. (ii) 2-Benzoyl-3-phenylacrylonitrile was synthesized by the aerobic oxidation of benzyl alcohol followed by the Knoevenagel condensation with benzoyl acetonitrile using three different non-polar solvents, i.e., toluene, benzene, and mesitylene. The conversion of benzyl alcohol was higher for the hybrid materials compared to the individual components but decreased with the increase of the graphene oxide concentration.

Flexible substrates have known increased popularity over rigid ones due to their use in surface-enhanced Raman scattering (SERS). They provide irregular surfaces, ideal for in situ sensing. In this context, we report the SERS performance of hybrid ZnO@Ag thin films deposited by magnetron sputtering (MS) on flexible, thermoplastic substrates. This physical deposition method is acknowledged for obtaining high-quality and reproducible ZnO films that can be embedded in (bio)sensing devices with various applications. Three types of thermoplastic-based, commercially available substrates with different glass transition temperatures (T_g) were chosen for the variation in flexibility, transparency, and thickness. Zeonor^® (T_g = 136 °C, thickness of 188 μm) and two types of Topas (Topas^®: T_g = 142 °C, thickness of 176 μm; Topas2: T_g = 78 °C, thickness of 140 μm) thermoplastic sheets are nonpolar and amorphous cyclo-olefin polymer (COP) and cyclo-olefin copolymers (COC), respectively. Their thicknesses and different values of T_g can greatly affect the topographical and roughness properties of films with small thicknesses and, thus, can greatly influence the enhancement of the Raman signal. The ZnO films deposited on top of Zeonor^® or Topas^® have identical morphological properties, as shown by the scanning electron microscopy (SEM) characterization. Subsequently, by using the MS technique, we tuned the thickness of the deposited silver (Ag) films in the range of 7–30 nm to assess the growth influence on the morphology and the SERS signal amplification of the substrates with and without the ZnO intermediate layer. The SEM analysis showed that the Ag atoms migrated both into the interstitial areas, filling the voids between the ZnO granular structures, and over the latter, forming, in this case, isolated Ag clusters. SERS analysis performed on the ZnO-Ag hybrid films using crystal violet (CV) molecule revealed a limit of detection (LOD) of 10⁻⁷ M in the case of 15 nm thick Ag/Zeonor^® interlayer films ZnO and relative standard deviation (RSD) below 10%.

Nodularin (NOD) is a potent toxin produced by Nodularia spumigena cyanobacteria. Usually, NOD co-exists with other microcystins in environmental waters, a class of cyanotoxins secreted by certain cyanobacteria species, which makes identification difficult in the case of mixed toxins. Herein we report a complete theoretical DFT-vibrational Raman characterization of NOD along with the experimental drop-coating deposition Raman (DCDR) technique. In addition, we used the vibrational characterization to probe SERS analysis of NOD using colloidal silver nanoparticles (AgNPs), commercial nanopatterned substrates with periodic inverted pyramids (Klarite^TM substrate), hydrophobic Tienta^® SpecTrim^TM slides, and in-house fabricated periodic nanotrenches by nanoimprint lithography (NIL). The 532 nm excitation source provided more well-defined bands even at LOD levels, as well as the best performance in terms of SERS intensity. This was reflected by the results obtained with the Klarite^TM substrate and the silver-based colloidal system, which were the most promising detection approaches, providing the lowest limits of detection. A detection limit of 8.4 × 10⁻⁸ M was achieved for NOD in solution by using AgNPs. Theoretical computation of the complex vibrational modes of NOD was used for the first time to unambiguously assign all the specific vibrational Raman bands.