Silicon/carbon nanotube (Si/CNTs) nanocomposite is a promising anode material for lithium ion batteries (LIBs). Challenges related to the tricky synthesis process, as well as the weak interaction between Si and CNTs, hinder practical applications. To address these issues, a facile, one-step method to synthesize Si/CNTs nanocomposite by using silica (SiO₂) as a reactant via a magnesium reduction process was developed. In this synthesis, the heat released enables the as-obtained Si to react with CNTs in the interfacial region to form silicon carbide (SiC). By virtue of the unique structure composed of Si nanoparticles strongly anchored to conductive CNTs network with stable Si–C chemical bonding, the Si/SiC/CNT nanocomposite delivers a stable capacity of ~1100 mAh g⁻¹ and a capacity retention of about 83.8% after 200 cycles at a current density of 100 mA g⁻¹. Our studies may provide a convenient strategy for the preparation of the Si/C anode of LIBs.

Silicon/carbon (Si/C) composite has been proven to be an effective method of enhancing the electrochemical performance of Si-based anodes for lithium-ion batteries (LIBs). However, the practical application of Si/C materials in LIBs is difficult because of the weak interaction between Si and C. In this study, we applied two-step diazotization reactions to modify graphite nanosheets (GNs) and Si nanoparticles (Si NPs), yielding a stable Si–Ar–GNs composite. Owing to aryl (Ar) group bonding, Si NPs were dispersed well on the GNs. The as-prepared Si–Ar–GNs composite delivered an initial reversible capacity of 1174.7 mAh·g⁻¹ at a current density of 100 mAh·g⁻¹. Moreover, capacity remained at 727.3 mAh·g⁻¹ after 100 cycles, showing improved cycling performance. This synthesis strategy can be extended to prepare other Si/C anode materials of LIBs.