Nanospheres and microspheres are known as a multipurpose compounds and are used in various branches of science. Recent controlled delivery systems for drugs are also based on poly-micro and nanospheres. In our study we describe an investigation of the influence of thermosensitive polymer N-isopropylacrylamide (NIPA) on the release of the drug naproxen sodium (NS) with a hydrogel hydroxypropyl methylcellulose (HPMC) base. The hydrodynamic diameter (D_H) of the obtained polymer was measured by using dynamic light scattering (DLS) at a wavelength of 678 nm. Hydrogel formulations of NS were prepared in a specific way ex tempore. NS was sprinkled on the surface of a distilled water, then polymer soluted in water was added. Afterward, HPMC was affixed to the solution. Prepared samples were stored at room temperature for 24 h. Release tests showed that modification of thevcross-linker type influenced the properties of synthesized polymeric particles. The NIPA derivatives obtained via surfactant free precipitation polymerization (SFPP) may be formulated as hydrogel preparations using HPMC. The obtained formulations presented varied half-release times, depending on the type of applied NIPA derivatives in hydrogel formulations. At 18 °C, the release rates were lower comparing to the reference HPMC hydrogel, whereas at 42 °C, the release rates were significantly higher. The synthesized thermosensitive polymers enabled temperature-triggered release of NS.

Poly-N-isopropylacrylamide (polyNIPA) is an extensively studied polymer in the field of controlled drug delivery. PolyNIPA contains carbonyl and amide groups along a hydrophobic chain. In an aqueous environment, crosslinked polyNIPA forms a gel characterized by a reversible volume phase transition temperature (VPTT), in response to changes in the external environment excited by the temperature factor. NIPA-based polymers were synthesized by a surfactant-free precipitation polymerization (SFPP) method at a temperature of 70 °C using the free radical initiator potassium persulfate (KPS) and at 35 °C using redox initiator system KPS with N,N,N’,N’-tetramethylethylenediamine (TEMED). The synthesized products were evaluated via dynamic light scattering (DLS), nuclear magnetic resonance (NMR) and Fourier-transform infrared spectroscopy (FTIR). The chemical structure, molecular mass, and hydrodynamic diameter of obtained particles, as well as the effects of synthesized polymers on the release of the active substance, naproxen sodium (NS), from hydroxypropyl methyl cellulose (HPMC)-based hydrogels were assessed. The use of the TEMED activator affected the particle size, as well as the release kinetics of NS. The insertion of TEMED into reactant mixtures may be applied to modify the release kinetics of NS from hydrogel preparations.