This review summarizes recent advances in self-healing PU by the “dynamic covalent bonding + X” method, where X represents dynamic covalent bonds, hydrogen bonding, metal coordination bonding, nanofillers and others.

One of the major obstacles for polyhydroxybutyrate (PHB), a biodegradable and biocompatible polymer, in commercial applications is its poor elongation at break (~3%). In this study, the effects of nanocellulose contents and their types, including cellulose nanocrystals (CNCs) and cellulose nanofibers (CNFs) on the crystallization, thermal, and mechanical properties of PHB composites were systematically compared. We explored the toughening mechanisms of PHB by adding CNCs and cellulose CNFs. The results showed that when the morphology of bagasse nanocellulose was rod-like and its content was 1 wt %, the toughening modification of PHB was the best. Compared with pure PHB, the elongation at break and Young’s modulus increased by 91.2% and 18.4%, respectively. Cellulose nanocrystals worked as heterogeneous nucleating agents in PHB and hence reduced its crystallinity and consequently improved the toughness of PHB. This simple approach could potentially be explored as a strategy to extend the possible applications of this biopolymer in packaging fields.

Deep eutectic solvents (DESs) is a newly developed green solvent with low cost, easy preparation and regeneration. Because of its excellent solubility and swelling effect in lignocellulose, it has received widespread attention and recognition. In this study, choline-based deep eutectic solvents (DESs)—choline chloride-urea (CC-U), choline chloride-ethylene glycol (CC-EG), choline chloride-glycerol (CC-G), choline chloride-lactic acid (CC-LA), and choline chloride-oxalic acid (CC-OA)—were used to extract and separate bagasse. The effects of hydrogen bond donors on lignin separation and the fiber and lignin structure were investigated. All five DESs could dissolve lignin from bagasse; acidic DESs exhibited higher solubility than basic DESs. CC-OA effectively separated lignin and hemicellulose. CC-LA showed weaker lignin separation ability than CC-OA. CC-G, CC-EG, and CC-U were more inclined to selectively separate lignin than hemicellulose. The crystalline cellulose II structure was retained after DES pretreatment. Acidic DESs effectively improved the crystallinity of bagasse fiber; the crystallinities for CC-OA and CC-LA pretreatment were 62.26% and 61.65%, respectively. The lignin dissolved in DES was mainly syringyl lignin. The lignin dissolved in CC-U, CC-LA, and CC-OA contained a small amount of guaiacyl lignin.