The susceptibility of rendering mortars to cracking is a complex phenomenon. Fibers have been incorporated in mortars to ensure the durability of the render and can improve the flexural strength, fracture toughness, and impact resistance of the mortars. Aside from the better cracking performance of fiber reinforced mortars, natural fibers have been a path to reducing the environmental impacts of construction materials. Recycling has high sustainability-related potential as it can both mitigate the amount of waste being inadequately disposed and reduce the consumption of natural raw materials. Studies on the incorporation of waste in civil engineering materials have been growing, and recycled fibers may be feasible to incorporate in mortars. Natural fibers are considered as a viable replacement for synthetic ones. Several studies have investigated vegetal fibers in cementitious composites. However, only a few have focused on the incorporation of waste animal-based fiber. The aim of this work is to analyze the feasibility of the use of natural sheep’s wool fibers on the reinforcement of mortars and in particular to improve their cracking behavior. For this purpose, two different binders were used: cement and cement-lime mortars were produced. The incorporation of 10% and 20% (in volume) of 1.5 cm and 3.0 cm wool fibers was analyzed. The results show that the incorporation of wool fibers increased the ductility of the mortars and improved their mechanical properties.

Coir fiber is a by-product waste generated in large scale. Considering that most of these wastes do not have a proper disposal, several applications to coir fibers in engineering have been investigated in order to provide a suitable use, since coir fibers have interesting properties, namely high tensile strength, high elongation at break, low modulus of elasticity, and high abrasion resistance. Currently, coir fiber is widely used in concrete, roofing, boards and panels. Nonetheless, only a few studies are focused on the incorporation of coir fibers in rendering mortars. This work investigates the feasibility to incorporate coir fibers in rendering mortars with two different binders. A cement CEM II/B-L 32.5 N was used at 1:4 volumetric cement to aggregate ratio. Cement and air-lime CL80-S were used at a volumetric ratio of 1:1:6, with coir fibers were produced with 1.5 cm and 3.0 cm long fibers and added at 10% and 20% by total mortar volume. Physical and mechanical properties of the coir fiber-reinforced mortars were discussed. The addition of coir fibers reduced the workability of the mortars, requiring more water that affected the hardened properties of the mortars. The modulus of elasticity and the compressive strength of the mortars with coir fibers decreased with increase in fiber volume fraction and length. Coir fiber’s incorporation improved the flexural strength and the fracture toughness of the mortars. The results emphasize that the cement-air-lime based mortars presented a better post-peak behavior than that of the cementitious mortars. These results indicate that the use of coir fibers in rendering mortars presents a potential technical and sustainable feasibility for reinforcement of cement and cement-air-lime mortars.

The construction sector is responsible for one third of the total wastes produced in the EU. Finding solutions for the reuse or recycling of these wastes is one of the major environmental concerns of modern times. The replacement of sand or cement in specific construction materials, such as concrete or mortars, is a possible solution for these wastes’ management. By using construction and demolition wastes in construction materials, namely on buildings, the cycle of circular economy is closed, increasing the life cycle of the wastes in the same sector. In this research, a reduction of cement content in rendering mortars is analysed. This reduction is achieved by a decrease of the cement/aggregate ratio simultaneously with the incorporation of very fine recycled aggregate from construction and demolition waste. Two recycled aggregates were studied: recycled concrete aggregate (RCA) and mixed recycled aggregate (MRA). The fresh and hardened state properties of the mortars were analysed. Several tests were carried out to evaluate the mortars’ performance, such as mechanical strength tests, water absorption tests, drying tests and shrinkage. It was noticed that the incorporation of RCA led to a better behaviour than in the reference mortar, in terms of mechanical strengths and protection against water.

This paper presents a study of incorporation of two types of construction and demolition waste (CDW) in rendering mortars, as aggregates at 0%, 20%, 50% and 100% (by volume). Recycled concrete aggregate (RCA) and mixed recycled aggregate (MRA) were used. The former is mainly composed of cementitious waste and the latter consists of a mixture of non-segregated wastes. The performance of the cement mortars with recycled aggregates was evaluated through an extensive experimental programme. The analysis comprised workability, mechanical strength, water absorption, shrinkage, open porosity and the evaluation of durability by permeability to water under pressure after an artificial accelerated ageing test. The results are considered positive, although as the incorporation of recycled aggregates (both MRA and RCA) increased the mechanical strength, the modulus of elasticity and bulk density decreased, which leads to the production of lighter mortars that are less susceptible to cracking. The modified mortar with 20% of MRA presented the best performance, in terms of mechanical behaviour.