A desirable microenvironment is essential for wound healing, in which an ideal moisture content is one of the most important factors. The fundamental function and requirement for wound dressings is to keep the wound at an optimal moisture. Here, we prepared serial polyurethane (PU) membrane dressings with graded water vapor transmission rates (WVTRs), and the optimal WVTR of the dressing for wound healing was identified by both in vitro and in vivo studies. It was found that the dressing with a WVTR of 2028.3 ± 237.8 g/m²·24 h was able to maintain an optimal moisture content for the proliferation and regular function of epidermal cells and fibroblasts in a three-dimensional culture model. Moreover, the dressing with this optimal WTVR was found to be able to promote wound healing in a mouse skin wound model. Our finds may be helpful in the design of wound dressing for wound regeneration in the future.

Extrusion-based bioprinting (EBB) holds potential for regenerative medicine. However, the widely-used bioinks of EBB exhibit some limitations for skin regeneration, such as unsatisfactory bio-physical (i.e., mechanical, structural, biodegradable) properties and compromised cellular compatibilities, and the EBB-based bioinks with therapeutic effects targeting cutaneous wounds still remain largely undiscussed. In this review, the printability considerations for skin bioprinting were discussed. Then, current strategies for improving the physical properties of bioinks and for reinforcing bioinks in EBB approaches were introduced, respectively. Notably, we highlighted the applications and effects of current EBB-based bioinks on wound healing, wound scar formation, vascularization and the regeneration of skin appendages (i.e., sweat glands and hair follicles) and discussed the challenges and future perspectives. This review aims to provide an overall view of the applications, challenges and promising solutions about the EBB-based bioinks for cutaneous wound healing and skin regeneration.

Spatial information has been shown to be critical for cell differentiation and function. Therefore, a better understanding of skin microstructures is very important for biomimetic and bioengineered scaffolds of engineering skin. The purpose of the study was to generate collagen/elastin-based three-dimensional (3D) images of human dermis to further understand the microstructures of the skin, which is believed to be helpful in the fabrication of bionic engineered skin. Skin samples were fixed, embedded, serially sectioned, stained with aldehyde-fuchsin, and photographed as serial panoramas. Dermal subregions were divided according to dermal depth and distance to hair follicle. The porosity, pore diameters, and wall thickness of human acellular dermal matrix (ADM) were measured by microcomputed tomography (micro-CT). Three-dimensional reconstructed images of collagen and elastic fibers were generated. Our results showed that there were fewer elastic fibers in the subregions close to hair follicles than in the subregions far away from hair follicles (p<0.001), but the collagen fibers were evenly distributed. Both collagen and elastic fibers were found in fewer numbers in the layers either close to the epidermis or close to the hypodermis. The mean proportions of collagen fibers and elastic fibers in the whole dermis were 28.96%±14.63% and 8.06%±3.75%, respectively. The porosity of ADM calculated by micro-CT was 68.3%±5.8%. The mean pore diameter of ADM was 131.2±96.8 μm, and the wall thickness of pores was 207.2±251.7 μm. This study represents for the first time that 3D histological cutaneous structures have been presented, which may be helpful for the next generation of skin engineering.