As the first batch of products after the resource utilization of construction and demolition waste, low-grade recycled aggregate (RA) has not been fully utilized, which hinders the development of the comprehensive recycling industry of construction waste. Therefore, this paper studies the mechanical properties of porous concrete (POC) with low-grade RA. An improved relationship between porosity and compressive strength of brittle, porous materials is used to express the compressive strength of POC with recycled aggregate (RPOC), and the prediction for compressive strength of porous concrete with low-grade RA is constructed by analyzing the mechanism of compressive damage. The results show: the compressive strength of porous concrete decreases with the addition of low-grade recycled aggregate, but the effect is not obvious when the replacement rate is less than 25%. The error range of the relationship between porosity and compressive strength of RPOC is basically within 15% after improvement. The prediction model for compressive strength based on the ideal sphere model of aggregate can accurately reflect the compressive strength of porous concrete with low-grade RA. The results of this study can provide a reference for the staff to learn about the functional characteristics of recycled products in advance and provide security for the actual project.

Traditional landfill disposal of muck uses a significant amount of land and pollutes the environment, while current solidification methods heavily depend on energy-intensive cement. This study introduces a novel approach for synergistically solidifying muck using cement, fly ash, and steel slag, aiming to utilize waste resources and achieve low-carbon disposal. Experimental optimization identified the optimal ratio (cement:fly ash:steel slag = 2:2:1). The findings indicate that cement is crucial for early strength, while industrial waste materials enhance long-term performance through continued reactions. At a total solidifying agent content of 4–6%, the material exhibits optimal mechanical properties and durability, with only a 4% strength loss after 12 dry–wet cycles. Microscopic analysis indicates that several gels and polymers with cementing properties are produced, collectively enhancing the material’s structure. Additionally, this material effectively immobilizes heavy metals, including chromium, lead, arsenic, and cadmium, with leaching concentrations that are well below safety thresholds. This approach provides a dependable and eco-friendly method for large-scale disposal of construction waste muck and industrial solid waste, offering significant potential for engineering applications. Further studies could investigate additional solid waste types and formulations suitable for high-moisture materials like sludge.