The nature is continually providing varied resources for creating textile materials for various applications. Although many textile fibers in the nature are provided with the fibrous kind itself it additionally offers raw materials that may be changed and formed into a filament in a way similar to the melt and solution spinning of other textile fibers. Basalt is an igneous rock, which is solidified volcanic lava. In recent years, basalt received attention as a replacement for asbestos fibers. Basalt has emerged as a contender in the fiber reinforcement of composites. Basalt fiber (BF) is capable to withstand very high temperature and can be used in high performance applications. This paper is review of state of art of knowledge of BF, the production methods, properties and its applications.

In recent years, in an attempt to substitute the conventional synthetic sound absorption material, natural fibers and their sound absorption properties have been increasingly studied. This is due to the fact that conventional synthetic fiber has potential health risks for human beings and significant environmental impact. In this review, existing and newly emerging natural fiber sound absorbers are summarized and highlighted in three categories: raw material, fiber assembly and composite. The sound absorption mechanism, several widely used prediction models and the popular acoustic characterization methods are presented. The comparison of sound absorption properties between some natural sound absorbers and glass fiber is conducted in two groups, i.e., thin material and thick material. It is found that many natural fibers have comparable sound absorption performance, some of them can be the ideal alternatives to glass fiber, such as kapok fiber, pineapple-leaf fiber and hemp fiber. Last, the conclusion part of this review gives an outlook regarding the promotion of the commercial use of natural fiber by means of theoretical study, efficient and environmentally friendly pretreatment and Life Cycle Assessment.

The use of acoustic panels is one of the most important methods for sound insulation in buildings. Moreover, it has become increasingly important to use green/natural origin materials in this area to reduce environmental impact. This study focuses on the investigation of acoustic, mechanical and thermal properties of natural fiber waste reinforced green epoxy composites. Three different types of fiber wastes were used, e.g., cotton, coconut and sugarcane with epoxy as the resin. Different fiber volume fractions, i.e., 10%, 15% and 20% for each fiber were used with a composite thickness of 3 mm. The sound absorption coefficient, impact strength, flexural strength, thermal conductivity, diffusivity, coefficient of thermal expansion and thermogravimetric properties of all samples were investigated. It has been found that by increasing the fiber content, the sound absorption coefficient also increases. The coconut fiber-based composites show a higher sound absorption coefficient than in the other fiber-reinforced composites. The impact and flexural strength of the cotton fiber-reinforced composite samples are higher than in other samples. The coefficient of thermal expansion of the cotton fiber-based composite is also higher than the other composites. Thermogravimetric analysis revealed that all the natural fiber-reinforced composites can sustain till 300 °C with a minor weight loss. The natural fiber-based composites can be used in building interiors, automotive body parts and household furniture. Such composite development is an ecofriendly approach to the acoustic world.

The paper reports experimental research regarding the mechanical characteristics of concrete reinforced with natural cellulosic fibers like jute, sisal, sugarcane, and coconut. Each type of natural fiber, with an average of 30 mm length, was mixed with a concrete matrix in varying proportions of 0.5% to 3% mass. The tensile and compressive strength of the developed concrete samples with cellulosic fiber reinforcement gradually increased with the increasing proportion of natural cellulosic fibers up to 2%. A further increase in fiber loading fraction results in deterioration of the mechanical properties. By using jute and sisal fiber reinforcement, about 11.6% to 20.2% improvement in tensile and compressive strength, respectively, was observed compared to plain concrete, just by adding 2% of fibers in the concrete mix. Bending strength increased for the natural fiber-based concrete with up to 1.5% fiber loading. However, a decrease in bending strength was observed beyond 1.5% loading due to cracks at fiber−concrete interface. The impact performance showed gradual improvement with natural fiber loading of up to 2%. The water absorption capacity of natural cellulosic fiber reinforced concrete decreased substantially; however, it increased with the loading percent of fibers. The natural fiber reinforced concrete can be commercially used for interior or exterior pavements and flooring slabs as a sustainable construction material for the future.