In this study, the powder-pack boriding process on low-carbon stainless steel was carried out at 1273 K for 4 h of exposure to obtain a layer around ~57 μm conformed by FeB, Fe2B, and others alloying elements. Firstly, the presence of iron borides formed on the surface of borided AISI 316L alloy was confirmed by optical microscopy combined with the X-ray diffraction analysis. After, the sensed Vickers indentation test was performed on the iron boride layer to estimate the behavior of hardness and Young’s modulus. Sliding wear tests on the borided AISI 316L alloy were performed according to the ASTM G133-05 standard procedure, with the following conditions: distances of 50 and 150 m, normal loads of 5 and 20 N, and a sliding speed of 30 mm/s. Finally, the results showed that the presence of FeB-Fe2B improves the resistance to wear around 41 times compared to the untreated material.

In the braking system, the heat dissipation generated by the friction between the disc and pad should be evacuated as quickly as possible. In this work, five common different automotive disc brakes were studied through mathematical theories of heat transfer and numerical methods using the ANSYS software. In addition, a direct comparison between experimental, theoretical, and simulation values found in the open literature was performed to propose a disc brake with an improved geometry in terms of dissipation of heat transfer. The numerical results were considered to propose two possible solutions of disc brake geometries using N-38 ventilation blades used in aeronautic engineering. An improvement in temperature dissipation was achieved by approximately 23.8% compared to the five geometries analyzed with a simple type N-38 ventilation blade. The heat dissipation in the brakes strongly depends on the geometry of the disc, the geometry of the blades, the material from which it is manufactured, the material of the pad, the weight of the vehicle, and the operating conditions, as can be verified with mathematical calculations and experiments. The results obtained demonstrate that the discs can be used effectively in extreme working conditions (80 km/h and 33°C), without affecting the safety of the occupants and the braking system.