Objectives: To assess the color stability and surface microhardness of Bulk-Fill composite materials available in the Saudi Arabia market. Methods: Five composite materials (Filtek Z350, Filtek Bulk-Fill, Tetric N-Ceram Bulk-Fill, Sonic Fill 2, and SDR) were investigated. Samples (n = 20; 10 mm in diameter and 2 mm in thickness) were fabricated using a stainless-steel mold and were immersed in tea, coffee, berry juice, and distilled water (control). Baseline (T₀) shades of specimens were recorded using a spectrophotometer and after 10 (T₁), 30 (T₂), 60 (T₃), and 90 days (T₄) of immersion. Measurements were obtained against a black background and CIE L*a*b* data was used to calculate ΔE for each group. Vickers microhardness values were obtained at T₀ and T₄. Data was analyzed using mixed model repeated measure ANOVA at 0.05 significance level. Results: Time, material, and solution effects have statistically significant effect on ΔE. Tea was the most staining solution. Z350 was associated with the highest ΔE values while SDR showed the lowest values. No other materials showed significant difference between each other. Solutions were statistically different from each other. All materials were different from each other regarding microhardness. Conclusion: Bulk-Fill materials showed more color stability but lower microhardness values compared to universal resin control.

The aim of this study was to compare color shift, color stability, and post-polishing surface roughness of esthetic restorative materials. Twenty-five disc-shaped specimens (10 mm in diameter and 2 mm in thickness) from five esthetic resin materials (Z250XT, IPS Empress-Direct, G-ænial, Vit-l-escence, and Ceram.X) were fabricated. Color shift before and immediately after light-curing (∆E₀) then color stability after immersion in tea, coffee, berry juice, and distilled water were measured using a spectrophotometer. Color changes were measured after 2 (ΔE₂), 4 (ΔE₄), 6 (ΔE₆), and 8 weeks (ΔE₈). Surface roughness values (Rq) were determined using an optical profilometer after polishing using a rotary polishing system. Data were analyzed using ANOVA and multiple comparison methods at 0.05 significance level. There were no significant differences between the tested materials regarding color shift except between Vit-l-escence and Ceram.X (p = 0.033). There was no significant difference between coffee and tea solutions (p = 1.0) and between berry juice and distilled water (p = 0.15). There was no difference between the tested materials regarding Rq (p = 0.057). Ceram.X was associated with the lowest ΔE₈ values overall. Tested materials were comparable regarding color shift and post-polishing surface roughness. Susceptibility to staining was dependent on the material.

The aim of this study was to test the antimicrobial properties of dental cements modified with magnesium oxide (MgO) nanoparticles. Zein-modified MgO nanoparticles (zMgO) in concentrations (0.0, 0.3, 0.5, and 1.0%) were mixed with dental cements (Fuji II, Rely X Temp E, Ionoglass Cem, Es Temp NE, and System P link). Eight discs were fabricated from each zMgO-cement pair for a total of 32 specimens for each cement. Characterization of the dental cements incorporating zMgO was done by X-ray Diffraction (XRD) and Field Emission Scanning Electron Microscopy (FESEM). The antimicrobial properties of the mixtures were tested using direct contact and agar diffusion assays against Streptococcus mutans, Staphylococcus aureus, Enterococcus faecalis, and Candida albicans. Data was analyzed using two-way analysis of variance and LSD post hoc test at 0.05 significance level. XRD spectra showed sharp peaks of zMgO indicating its high crystalline nature, while the amorphous dental cements with zMgO had broad peaks. FESEM analysis showed a uniform distribution of the zMgO nanoparticles in the cement. There were significant inhibition zone values associated with all concentrations of zMgO-cement mixtures tested compared to controls (p < 0.001) with a dose-response recorded only with Fuji II. Optical density values were significantly lower in zMgO groups compared to controls for all microorganisms. The effect was most prominent with Rely X against C. albicans and S. aureus. Dental cements containing zMgO showed significant antimicrobial properties that were dependent on the specific initial cement substrate.

The use of photo-curable resin composite restorations is an essential treatment modality in modern dental practice. The success and longevity of these restorations depend on achieving predictable and effective polymerization. Understanding the dynamics of the polymerization and the effect of light cure units (LCUs) on this process is paramount. The goal of this concise narrative review is to provide a simplified presentation of basic principles of composite chemistry, polymerization reactions, and photo-curing with relevant terminologies. Clinical guidelines for choosing and maintaining LCUs, as well as safety precautions and factors under the control of the clinician are listed. Finally, clinical recommendations of LCUs’ usage and monitoring are included to aid practitioners in achieving predictable polymerization during the placement of direct resin composite restorations.

Bulk-fill (BF) dental resin composites are made to be polymerized in increments of up to 5 mm rather than the 2 mm increment recommended for conventional composites. This project aimed to determine microhardness (MH) profiles of BF resin composites at different depths and varying light cure (LC) distances from the light source in an attempt to mimic varying clinical situations. Forty-eight cylindrical specimens (4 mm diameter and 6 mm height) were prepared from 3 BF composites: Tetric N-Ceram Bulk-Fill (TBF), Filtek One Bulk-Fill (FBF), and Sonic-Fill 2 (SF2). Four different distances (0, 2, 4, and 6 mm) from the LC unit were investigated. Vickers MH was measured at the top and bottom of the samples and at every 1 mm, by creating 3 indentations at each depth. The bottom-top microhardness ratio (MHR) and percentage reduction in MHR were also measured. Data was analyzed using mixed-model repeated-measure ANOVA at 0.05 significance level. The main variables effects “material, LC distance, and depth” were significant (p < 0.001). Increasing LC distance and the depth of the tested BF significantly affected Vickers MH and MHR. None of the tested BF materials had sufficient MHR at the depths of 4–6 mm. SF2 showed the least MHR reduction.