Widespread use of Mg-Zn-Ca alloys in clinical orthopedic practice requires improvement of their mechanical properties—in particular, ductility—and enhancement of their bioactivity for accelerated osteoreconstruction. The alloy was studied in two structural states: after homogenization and after equal-channel angular pressing. Immersion and potentiodynamic polarization tests showed that the corrosion rate of the alloy was not increased by deformation. The mass loss in vivo was also statistically insignificant. Furthermore, it was found that deformation did not compromise the biocompatibility of the alloy and did not have any significant effect on cell adhesion and proliferation. However, an extract of the alloy promoted the alkaline phosphatase activity of human mesenchymal stromal cells, which indicates osteogenic stimulation of cells. The osteoinduction of the deformed alloy significantly exceeded that of the homogenized one. Based on the results of this work, it can be concluded that the alloy Mg-1%Zn-0.3%Ca modified by equal-channel angular pressing is a promising candidate for the manufacture of biodegradable orthopedic implants since it stimulates osteogenic differentiation and has greater ductility, which provides it with a competitive advantage in comparison with the homogenized state.

The effect of high-pressure torsion (HPT) on the microstructure, phase composition, mechanical characteristics, degradation rate, and bioactive properties of the Zn–1%Mg alloy is studied. An ultrafine-grained (UFG) structure with an average grain size of α-Zn equal to 890 ± 26 nm and grains and subgrains of the Mg₂Zn₁₁ and MgZn₂ phases with a size of 50–100 nm are formed after HPT. This UFG structure leads to an increase in the ultimate tensile strength of the alloy by ~3 times with an increase in elongation to 6.3 ± 3.3% due to the formation of a basal texture. The study of corrosion resistance did not show a significant effect of HPT on the degradation rate of the alloy. In addition, no significant changes in the bioactivity of the alloy after HPT: hemolysis, cellular colonization and Escherichia coli growth inhibition.

A study of the effect of rotary swaging (RS) on the microstructure and properties of the pre-extruded and pre-quenched Cu-0.5%Cr-0.08%Zr alloy was performed. RS leads to the formation of an ultrafine-grained (UFG) microstructure. UFG structure formation caused by RS increases the ultimate tensile strength (UTS) up to 443 ± 5 MPa and 597 ± 9 MPa for pre-quenched and pre-extruded alloys, respectively. Additionally, the reduction in ductility occurs after RS. It should be noted that UTS is increased for a pre-quenched alloy, while the strength of a pre-extruded alloy is dropped. The growth of UTS for the pre-quenched alloy is associated with the precipitation of fine Cr particles, whereas the recovery processes in the pre-extruded alloy induce the reduction in its UTS. An additional advantage of RS is an increase in the fatigue limit of the pre-quenched alloy up to 265 MPa, and of the pre-extruded alloy up to 345 MPa. The combination of extrusion and RS allows for the increase of the UTS of the Cu-0.5%Cr-0.08%Zr alloy up to 597 ± 9 MPa, while the levels of ductility and electrical conductivity are 10.9 ± 0.9% and 82.0 ± 1.7% IACS, respectively.

An attempt to improve the functional characteristics of a degradable Fe-Mn-5Si shape memory alloy by means of structure refinement by equal-channel angular pressing (ECAP) was made. In the course of ECAP, an austenitic ultrafine-grained structure was obtained. In shear bands with a thickness of 301 ± 31 nm, twins 11 ± 1 nm in size were formed. Due to the resulting structure, the tensile strength was doubled up to 1419 MPa, and the yield strength was increased up to 1352 MPa, four times higher compared with the annealed state. Dynamic indentation tests revealed a decrease in Young’s modulus by more than 2.5 times after ECAP compared to values measured in the annealed state. The results of the study of hemolytic and cytotoxic activity in vitro, as well as the local and systemic reactivity of the body of laboratory animals after implantation of the test samples indicate the biocompatibility of the alloy after ECAP. Biocompatibility, high specific strength and low modulus of elasticity open prospects for Fe-Mn-5Si alloy after ECAP to be used for the production of degradable implants that can effectively provide the fastening function in osteoreconstruction.