Porous metal membranes have recently received increasing attention, and significant progress has been made in their preparation and characterisation. This progress has stimulated research in their applications in a number of key industries including wastewater treatment, dairy processing, wineries, and biofuel purification. This review examines recent significant progress in porous metal membranes including novel fabrication concepts and applications that have been reported in open literature or obtained in our laboratories. The advantages and disadvantages of the different membrane fabrication methods were presented in light of improving the properties of current membrane materials for targeted applications. Sintering of particles is one of the main approaches that has been used for the fabrication of commercial porous metal membranes, and it has great advantages for the fabrication of hollow fibre metal membranes. However, sintering processes usually result in large pores (e.g., >1 µm). So far, porous metal membranes have been mainly used for the filtration of liquids to remove the solid particles. For porous metal membranes to be more widely used across a number of separation applications, particularly for water applications, further work needs to focus on the development of smaller pore (e.g., sub-micron) metal membranes and the significant reduction of capital and maintenance costs.

The influence of temperature on the forming behavior of an aluminum/polypropylene/aluminum (APA) sandwich sheet was studied. Shear and tensile tests were performed to determine the mechanical properties of the laminate and the component materials as a function of process temperature. The forming limit diagram (FLD) of the laminate was established for two different temperatures, and its springback behavior was examined in four-point bend and channel bend tests. Cup forming tests were performed at various test temperatures to determine the limiting drawing ratio (LDR) and the tendency for wrinkling at these temperatures. Although there was only a minor influence of temperature on the mechanical properties and the FLD values of the laminate, the bend test results reveal that springback can be reduced by forming at higher temperature. The decreasing strength of the core material with rising process temperature led to an increased tendency of the laminate to wrinkle in the heated cup drawing tests.