ZIF-8 nanoparticle-doped polyvinyl alcohol (PVA)-S-MC films were prepared via casting method. The effect of different concentrations of ZIF-8 on the physical properties and structural characterization of the films were investigated. The results indicated that ZIF-8 could increase the water resistance and mechanical property of the membrane. Through FTIR, scanning electron microscope (SEM), atomic force microscope (AFM), and TGA analysis, it was found that ZIF-8 changed the phenomenon of macromolecule agglomeration and improved the thermal stability of the membrane. The breathable behavior of the film was also studied through oxygen permeability and water vapor permeability analysis. The result illustrated that the breathability of the film improved significantly by adding ZIF-8. The maximum reached when the weight ratio of ZIF-8 was 0.01 wt %. The property expands the application of PVA/starch blend film in the postharvest technology of fruits and vegetables.

In order to reduce the fire risk of rigid polyurethane foams (RPUF), three kinds of zeolitic imidazolate frameworks (ZIFs) were prepared. The results of Fourier transform infrared spectroscopy (FTIR), scanning electron microscope (SEM and X-ray diffraction (XRD) showed that ZIFs were successfully prepared. The combustion test results showed that the heat and smoke production of the composite containing ZIFs was obviously reduced. In particular, the peak heat release rate (PHRR) of ZIF-8/RPUF decreased from 740.85 kW/m² (Ref. RPUF) to 489.56 kW/m², while the PHRR of ZIF-7/RPUF and ZIF-11/RPUF is 598.39 and 583.36 kW/m², respectively. The addition of ZIFs improved the thermostability of the composite. The T50% of ZIF-8/RPUF, ZIF-7/RPUF and ZIF-11/RPUF increased to 364, 382 and 380 °C, respectively. The maximum light absorption of ZIF-7/RPUF and ZIF-11/RPUF was about 88%, which is higher than that of ZIF-8/RPUF (75%). The results of Raman spectroscopy showed that the I_D/I_G value of Ref. RPUF is 2.96, while the I_D/I_G value of ZIFs/RPUF reduces to less than 2.80. The main mechanism of ZIFs for reducing the fire risk of RPUF was the catalysis and incarbonization of ZIFs during combustion based on the results of thermogravimetric analysis and Raman spectroscopy of char residue.