Black poplar (Populus nigra L.) was thermally modified in nitrogen atmosphere. The effects of the modification process on poplar wood were evaluated for temperatures: 160 °C, 190 °C, and 220 °C applied for 2 h; and 160 °C and 190 °C for 6 h. The percentual impact of temperature and time of modification on the properties of modified wood was analysed. The study permitted the identification correlations between the chemical composition and selected physical properties of thermally modified poplar wood. The dimensional stability of poplar wood was improved after thermal modification in nitrogen. The higher the temperature of modification, the lower the equilibrium moisture content (EMC) of black poplar. At the temperature of 220 °C, EMC was two times lower than the EMC of non-modified black poplar. It is also possible to reduce the dimensional changes of wood two-fold (at the modification temperature of 220 °C), both in radial and tangential directions, independently of the acclimatization conditions (from 34% to 98% relative humidity, RH). Similar correlations have been found for wood that has been soaked in water. Higher modification temperatures and longer processing times contributed to a lower swelling anisotropy (SA).

Scots pine (Pinus sylvestris L.) is a widespread species throughout Europe and at the same time is dominant in Polish forests and of key importance in the wood industry. Pine stands are subjected to numerous environmental stresses, and one of them is the different physico-chemical and biological properties of post-agricultural soils compared to forest soils, which may affect the properties of the resulting wood and its industrial suitability. The research material taken at the height of 1.3 m from tree trunks (breast height diameter, dbh) in the form of sections and discs was collected in an 80-year-old pine stand from four plots, representing former agricultural and ancient forest land, and two types of habitats: fresh coniferous forest and fresh mixed coniferous forest. The forest habitat trophy had a decisive impact on the dendrometric characteristics and properties of pine wood (density, modulus of elasticity, bending strength, and compressive strength along the tracheids). The history of soil use (post-agricultural or forestry) did not affect the analyzed pine wood properties. Regardless of the forest habitat type and soil type history, pine wood at the dbh height showed a variability of features typical of century-old cultivated stands. Individual pine trunks were characterized by significant individual variability.

This work contains the preliminary results of research into the technical quality of the wood from Scots pine trees of diverse genetic origin, grown on an experimental plot at the Forest Experimental Station in Rogów. The following are the parent stands, numbered: 5 (the Tucholskie Forest 130 m a.s.l.), 7 (the Napiwodzko–Ramuckie Forest 145 m a.s.l.), 10 (the Piska Forest 145 m a.s.l.), 12 (the Biała Forest 95 m a.s.l.), 13 (the Namysłowsko–Ostrzeszowskie Forest 190 m a.s.l.), 15 (the Knyszyńska Forest 165 m a.s.l.), and 16 (the Nowotarskie Forest 590 m a.s.l.). The tested wood was obtained in 2018 from trees aged 52 years. The research material came from 100 trees in total. After felling, two logs approximately 0.5 m in length were cut from each tree. The height on the tree from which the material was taken ranged from breast height (1.3 m) to approximately 2.5 m. Next, planks were cut from the logs in a north–south direction; these were precisely described and then left to season. The work included the measurement and statistical analysis of one physical property, wood density (kg/m³), and of the following mechanical properties: compressive strength along the fibres, Rc₁₂ (MPa); static bending strength, Rg₁₂ (MPa); modulus of elasticity under static bending, Eg₁₂ (MPa); and indices of strength quality of the tested mechanical properties, JRc₁₂, JRg₁₂, and JEg₁₂ (km). The origin of the logs was shown to have a significant influence on wood density, compressive strength, static bending strength, and modulus of elasticity under static bending. The highest mean density was found for trees originating from stand 10 (537 kg/m³). The highest values of compressive strength were obtained for trees originating from stands 5 (45 MPa), and the highest static bending strength and modulus of elasticity under static bending were obtained for trees originating from stand 12 (102 and 9825 MPa, respectively).

Fast-growing poplar trees from plantations are the source of inexpensive wood that is intended mainly for chemical processing in the pulp and paper industry. Their potential as raw material for biofuel manufacturing is widely discussed as well. The detailed chemical composition of this raw material is therefore an important question. Five species of poplars were investigated: Populus alba, P. maximowiczii, P. trichocarpa, P. nigra, and P. tremula. Wood is a material consisting mainly of lignocellulose, but there are also many extractives. In temperate zone climate they typically represent up to 5% of wood mass. Their identification is difficult, due to various classes of compounds and great number of individual ones. These compounds can affect the properties of wood—its resistance to biotic agents and suitability to enzymatic treatment towards biofuels. Gas chromatography coupled with mass spectrometer (GC-MS) was used to analysis of extractives in various species of poplar wood. Compounds from several classes were identified like phenols, fatty acids, and their derivatives, sterols. Their identification was discussed along with estimation of their content in wood of investigated species.

Wood species from Africa, South America and Europe, primarily used as a flooring and construction material, were acquired for the study. Wetabillity was determined using the measurement of the contact angle of wood with the reference...

Transport of wood biomass is one of the key operations in forestry and in the wood industry. An important part is the transport of shredded wood, where the most common forms are chips and sawdust. The aim of the research was to present the variability of the total weight of trucks (gross vehicle weight, GVW), the weight of the empty trucks (tare), and loads of chips and sawdust in different periods of the year. Changes in specific parameters were analyzed: GVW; tare weight; trailer capacity; use of the trailer load capacity; bulk volume and bulk density of wood biomass loads; solid cubic meter (m³) and weight of 1m³ of the load; and load weight depending on the season, with simultaneous measurements of wood chips and sawdust moisture. More than 250 transports from four seasons of the year were analyzed in the research. It was found that the total weight of trucks (GVW) was at a comparable level, on average from 39.42 to 39.64 Mg with slight differences (with SD 0.29 and 0.39). The weight of empty trucks was 16.15 Mg for chip-bearing trucks and 15.93 Mg for sawdust-bearing trucks (with SD 0.604 and 0.526). The type of wood material has an influence on the transported volume. The average quantity of load in the bulk cubic meter was 64.783 m³ for wood chips (SD 3.127) and 70.465 m³ (SD 2.516) for sawdust. Over 30% differences in the volume of transported wood chips and approximately 18% for sawdust were observed. The use of the loading capacity of the trailer was on average 72.58% (SD 5.567) for the transport of wood chips and 77.42% (SD 3.019) for the transport of sawdust. The sawdust bulk density was from 0.3050 to 0.4265 Mg⋅m⁻³ for wood chips and 0.3200 to 0.3556 Mg⋅m⁻³ for sawdust. This parameter is significantly dependent on moisture content, and the determined correlation functions can be used for estimating and predicting bulk density. The abovementioned absolute moisture content of chips and sawdust also depends on the season, which also affects the selected parameters of wood biomass loads.