Telling Hexanes Apart: The efficiency of modern internal combustion engines depends on the relative reactivity of the hydrocarbons that comprise the fuel. In particular, branched hydrocarbons are less likely than their linear counterparts to react prematurely—a property reflected in the fuel mixture's octane number. Herm et al. (p. 960 ) report a metal organic framework material with triangular pore channels that discriminate among the differently shaped isomers of hexane more finely than the commercial standard.

Reactions between the tritopic pyrazole-based ligand 1,3,5-tris(1H-pyrazol-4-yl)benzene (H₃BTP) and transition metal acetate salts in DMF afford microporous pyrazolate-bridged metal–organic frameworks of the type M₃(BTP)₂·xsolvent (M = Ni (1), Cu, (2), Zn (3), Co (4)). Ab-initioX-ray powder diffraction methods were employed in determining the crystal structures of these compounds, revealing 1 and 2 to exhibit an expanded sodalite-like framework with accessible metal cation sites, while 3 and 4 possess tetragonal frameworks with hydrophobic surfaces and narrower channel diameters. Compounds 1–4 can be desolvated without loss of crystallinity by heating under dynamic vacuum, giving rise to microporous solids with BET surface areas of 1650, 1860, 930 and 1027 m² g⁻¹, respectively. Thermogravimetric analyses and powder X-ray diffraction measurements demonstrate the exceptional thermal and chemical stability of these frameworks. In particular, 3 is stable to heating in air up to at least 510 °C, while 1 is stable to heating in air to 430 °C, as well as to treatment with boiling aqueous solutions of pH 2 to 14 for two weeks. Unexpectedly, 2 and 3 are converted into new crystalline metal–organic frameworks upon heating in boiling water. With the combination of stability under extreme conditions, high surface area, and exposed metal sites, it is anticipated that 1 may open the way to testing metal–organic frameworks for catalytic processes that currently employ zeolites.

Colloidal nanocrystals (NCs) of APbX₃-type lead halide perovskites [A = Cs⁺, CH₃NH₃⁺ (methylammonium or MA⁺) or CH(NH₂)₂⁺ (formamidinium or FA⁺); X = Cl^–, Br^–, I^–] have recently emerged as highly versatile photonic sources for applications ranging from simple photoluminescence down-conversion (e.g., for display backlighting) to light-emitting diodes. From the perspective of spectral coverage, a formidable challenge facing the use of these materials is how to obtain stable emissions in the red and infrared spectral regions covered by the iodide-based compositions. So far, red-emissive CsPbI₃ NCs have been shown to suffer from a delayed phase transformation into a nonluminescent, wide-band-gap 1D polymorph, and MAPbI₃ exhibits very limited chemical durability. In this work, we report a facile colloidal synthesis method for obtaining FAPbI₃ and FA-doped CsPbI₃ NCs that are uniform in size (10–15 nm) and nearly cubic in shape and exhibit drastically higher robustness than their MA- or Cs-only cousins with similar sizes and morphologies. Detailed structural analysis indicated that the FAPbI₃ NCs had a cubic crystal structure, while the FA_0.1Cs_0.9PbI₃ NCs had a 3D orthorhombic structure that was isostructural to the structure of CsPbBr₃ NCs. Bright photoluminescence (PL) with high quantum yield (QY > 70%) spanning red (690 nm, FA_0.1Cs_0.9PbI₃ NCs) and near-infrared (near-IR, ca. 780 nm, FAPbI₃ NCs) regions was sustained for several months or more in both the colloidal state and in films. The peak PL wavelengths can be fine-tuned by using postsynthetic cation- and anion-exchange reactions. Amplified spontaneous emissions with low thresholds of 28 and 7.5 μJ cm^–2 were obtained from the films deposited from FA_0.1Cs_0.9PbI₃ and FAPbI₃ NCs, respectively. Furthermore, light-emitting diodes with a high external quantum efficiency of 2.3% were obtained by using FAPbI₃ NCs.

Bright green emitters with adjustable photoluminescence (PL) maxima in the range of 530–535 nm and full-width at half-maxima (fwhm) of <25 nm are particularly desirable for applications in television displays and related technologies. Toward this goal, we have developed a facile synthesis of highly monodisperse, cubic-shaped formamidinium lead bromide nanocrystals (FAPbBr₃ NCs) with perovskite crystal structure, tunable PL in the range of 470–540 nm by adjusting the nanocrystal size (5–12 nm), high quantum yield (QY) of up to 85% and PL fwhm of <22 nm. High QYs are also retained in films of FAPbBr₃ NCs. In addition, these films exhibit low thresholds of 14 ± 2 μJ cm^–2 for amplified spontaneous emission.