The application of modified spinel materials in commercial systems relates to the verification of their parameters under different conditions. Hence, in this study, the influence of temperature on the electrochemical behavior of sulfur-doped spinel (LiMn₂O_3.97S_0.03), with reference to stoichiometric spinel (LiMn₂O₄), was investigated. The electrochemical characteristics of Li-ion cells based on the fabricated spinels were investigated using galvanostatic charge–discharge tests (GCDT), cyclic voltammetry (CV), and electrochemical impedance spectroscopy (EIS). The results show that introducing sulfur into the spinel structure improves the electrochemical properties at each of the studied temperatures (3, 22 and 61 °C). LiMn₂O_3.97S_0.03 exhibits higher specific capacities, enhanced diffusivity and charge–discharge rates (particularly at low temperatures), and much better cycling stability, regardless of the testing conditions. Our research proves that an S-doping system is a better alternative to LiMn₂O₄ in the context of working parameters, while maintaining environmental friendliness and low manufacturing costs.

The influence of the pyrolysis temperature on the structural, textural, and electrochemical properties of carbon aerogels obtained from potato, maize, and rice starches was analyzed. The carbonization of organic precursors, followed by gelatinization, exchange of solvent, and drying process, was carried out in an argon atmosphere at temperatures ranging from 600 °C to 1600 °C. The nanostructured carbons were characterized by X-ray powder diffraction (XRD) as well as N2-adsorption/desorption (N2-BET) methods. The electrochemical behavior of Li-ion cells based on the fabricated carbon anodes was investigated using the galvanostatic charge/discharge tests (GCDT) and electrochemical impedance spectroscopy (EIS). The results show that the thermal treatment stage has a crucial impact on the proper formation of the aerogel material’s porous structures and also on their working parameters as anode materials. The highest relative development of the external surface was obtained for the samples pyrolysed at 700 °C, which exhibited the best electrochemical characteristics (the highest specific capacities as well as the lowest charge transfer resistances).

Among all advanced anode materials, graphite is regarded as leading and still-unrivaled. However, in the modern world, graphite-based anodes cannot fully satisfy the customers because of its insufficient value of specific capacity. Other limitations are being nonrenewable, restricted natural graphite resources, or harsh conditions required for artificial graphite production. All things considered, many efforts have been made in the investigation of novel carbonaceous materials with desired properties produced from natural, renewable resources via facile, low-cost, and environmentally friendly methods. In this work, we obtained N-doped, starch-based carbon aerogels using melamine and N₂ pyrolysis as the source of nitrogen. The materials were characterized by X-ray powder diffraction, elemental analysis, X-ray photoelectron spectroscopy, galvanostatic charge–discharge tests, cyclic voltammetry, and electrochemical impedance spectroscopy. Depending on the doping method and the nitrogen amount, synthesized samples achieved different electrochemical behavior. N-doped, bioderived carbons exhibit far better electrochemical properties in comparison with pristine ones. Materials with the optimal amount of nitrogen (such as MCAGPS-N8.0%—carbon aerogel made from potato starch modified with melamine and CAGPS-N1.2%—carbon aerogel made from potato starch modified by N₂ pyrolysis) are also competitive to graphite, especially for high-performance battery applications. N-doping can enhance the efficiency of Li-ion cells mostly by inducing more defects in the carbon matrix, improving the binding ability of Li⁺ and charge-transfer process.

In this work, we investigated the influence of gum arabic (GA) as a structuring additive, on the electrochemical behavior of bio-derived carbon aerogels (CAGs). Modified carbonaceous materials were prepared by the gelatinization process of potato starch (PS) with the addition of GA in various quantities, followed by the thermal treatment of the obtained gels in an inert gas atmosphere. The obtained anode materials were examined by X-ray diffraction (XRD), elemental analysis (EA), galvanostatic charge/discharge tests (GCDT), extensive cycling (LT-GCDT) and cyclic voltammetry (CV) methods. The highest electrochemical performance was achieved for carbon aerogel material, in which 1% w/w GA was added. The results showed that the proper composition of carbon precursor with a structuring promoter improves the rheological properties of starch gel and stabilizes the final aerogel structure affecting CAG functional properties.