Fused deposition modelling (FDM) is the most widely used additive manufacturing process in customised and low-volume production industries due to its safe, fast, effective operation, freedom of customisation, and cost-effectiveness. Many different thermoplastic polymer materials are used in FDM. Acrylonitrile butadiene styrene (ABS) is one of the most commonly used plastics owing to its low cost, high strength and temperature resistance. The fabricated FDM ABS parts commonly work under thermo-mechanical loads in actual practice. For producing FDM ABS components that show high fatigue performance, the 3D printing parameters must be effectively optimized. Hence, this study evaluated the bending fatigue performance for FDM ABS beams under different thermo-mechanical loading conditions with varying printing parameters, including building orientations, nozzle size, and layer thickness. The combination of three building orientations (0°, ±45°, and 90°), three nozzle sizes (0.4, 0.6, and 0.8 mm) and three-layer thicknesses (0.05, 0.1, and 0.15 mm) were tested at different environmental temperatures ranging from 50 to 70 °C. The study attempted to find the optimal combination of the printing parameters to achieve the best fatigue behaviour of the FDM ABS specimen. The experiential results showed that the specimen with 0° building orientation, 0.8 mm filament width, and 0.15 mm layer thickness vibrated for the longest time before the fracture at each temperature. Both a larger nozzle size and thicker layer height can increase the fatigue life. It was concluded that printing defects significantly decreased the fatigue life of the 3D-printed ABS beam.

The present paper aims to investigate the process parameters and damping behaviour of the acrylonitrile butadiene styrene (ABS) cantilever beam manufactured using material extrusion (MEX). The research outcome could guide the manufacture of MEX structures to suit specific operating scenarios such as energy absorption and artificially controlled vibration responses. Our research used an experimental approach to examine the interdependencies between process parameters (nozzle size, infill density and pattern) and the damping behaviour (first-order modal damping ratio and loss factor). The impact test was carried out to obtain the damping ratio from the accelerometer. A dynamic mechanical analysis was performed for the loss factor measurement. The paper used statistical analysis to reveal significant dependencies between the process parameters and the damping behaviour. The regression models were also utilised to evaluate the mentioned statistical findings. The multiple third-order polynomials were developed to represent the relation between process parameters and modal damping ratio using stiffness as the mediation variable. The obtained results showed that the infill density affected the damping behaviour significantly. Higher infill density yielded a lower damping ratio. Nozzle size also showed a notable effect on damping. A high damping ratio was observed at a significantly low value of nozzle size. The results were confirmed using the theoretical analysis based on the underlying causes due to porosity in the MEX structure.

Three-dimensional (3D) printing is one of the significant industrial manufacturing methods in the modern era. Many materials are used for 3D printing; however, as the most used material in fused deposition modelling (FDM) technology, acrylonitrile butadiene styrene (ABS) offers good mechanical properties. It is perfect for making structures for industrial applications in complex environments. Three-dimensional printing parameters, including building orientation, layers thickness, and nozzle size, critically affect the crack growth in FDM structures under complex loads. Therefore, this paper used the dynamic bending vibration test to investigate their influence on fatigue crack growth (FCG) rate under dynamic loads and the Paris power law constant C and m. The paper proposed an analytical solution to determine the stress intensity factor (SIF) at the crack tip based on the measurement of structural dynamic response. The experimental results show that the lower ambient temperature, as well as increased nozzle size and layer thickness, provide a lower FCG rate. The printing orientation, which is the same as loading, also slows the crack growth. The linear regression between these parameters and Paris Law’s coefficient also proves the same conclusion.

Acrylonitrile butadiene styrene (ABS) offers good mechanical properties and is effective in use to make polymeric structures for industrial applications. It is one of the most common raw material used for printing structures with fused deposition modeling (FDM). However, most of its properties and behavior are known under quasi-static loading conditions. These are suitable to design ABS structures for applications that are operated under static or dead loads. Still, comprehensive research is required to determine the properties and behavior of ABS structures under dynamic loads, especially in the presence of temperature more than the ambient. The presented research was an effort mainly to provide any evidence about the structural behavior and damage resistance of ABS material if operated under dynamic load conditions coupled with relatively high-temperature values. A non-prismatic fixed-free cantilever ABS beam was used in this study. The beam specimens were manufactured with a 3D printer based on FDM. A total of 190 specimens were tested with a combination of different temperatures, initial seeded damage or crack, and crack location values. The structural dynamic response, crack propagation, crack depth quantification, and their changes due to applied temperature were investigated by using analytical, numerical, and experimental approaches. In experiments, a combination of the modal exciter and heat mats was used to apply the dynamic loads on the beam structure with different temperature values. The response measurement and crack propagation behavior were monitored with the instrumentation, including a 200× microscope, accelerometer, and a laser vibrometer. The obtained findings could be used as an in-situ damage assessment tool to predict crack depth in an ABS beam as a function of dynamic response and applied temperature.

Acrylonitrile butadiene styrene (ABS) is the most commonly used thermoplastic printing material for fused deposition modelling (FDM). FDM ABS can be used in a variety of complex working environments. Notably, the thermo-mechanical coupled loads under complex operating conditions may lead to cracking and ultimately catastrophic structural failure. Therefore, it is crucial to determine the crack depth and location before a structural fracture occurs. As these parameters affect the dynamic response of the structure, in this study, the fundamental frequency and displacement amplitude response of a cracked 3D-printed ABS cantilever beam in a thermal environment were analytically and experimentally investigated. The existing analytical model, specifically the torsional spring model used to calculate the fundamental frequency change to determine the crack depth and location was enhanced by the proposed Khan-He model. The analytical relationship between the displacement amplitude and crack was established in Khan-He model and validated for the first time for FDM ABS. The results show that a reduced crack depth and location farther from the fixed end correspond to a higher fundamental frequency and displacement amplitude. An elevated ambient temperature decreases the global elastic modulus of the cracked beam and results in a lower fundamental frequency. Moreover, a non-monotonic relationship exists between the displacement amplitude and ambient temperature. The displacement amplitude is more sensitive to the crack change than the fundamental frequency in the initial stages of crack growth.