Metal organic frameworks (MOFs) have been rapidly developed in the application of electrode materials due to their controllable morphology and ultra-high porosity. In this research, flower-like layered nickel-based bimetallic MOFs microspheres with different metal central ions were synthesized by solvothermal method. Compared with Ni-MOFs, the optimization of the specific capacitance of NiCo-MOFs and NiMn-MOFs was been confirmed. For example, the specific capacitance of NiCo-MOFs can reach 882 F·g⁻¹ at 0.5 A·g⁻¹ while maintaining satisfactory cycle life (the specific capacity remains 90.1% of the initial value after 3000 charge-discharge cycles at 5 A·g⁻¹). In addition, the NiCo-MOFs//AC HSCs, which are composed of NiCo-MOFs and activated carbon (AC), achieved a maximum energy density of 18.33 Wh·kg⁻¹ at a power density of 400 W·kg⁻¹, and showed satisfactory cycle life (82.4% after 3000 cycles). These outstanding electrochemical properties can be ascribed to the synergistic effect between metal ions, the optimized conductivity, and the unique layered stacked flower structure, which provides a smooth transmission channel for electrons/ions. In addition, this research gives a general method for the application of MOFs in the field of supercapacitors.

This paper reports on the preparation, characterization, and catalytic properties of the Pd@UIO-66 for toluene oxidation. The samples are prepared by the double-solvent method to form catalysts with large specific surface area, highly dispersed Pd⁰ (Elemental palladium) and abundant adsorbed oxygen, which are characterized by X-ray Photoelectron Spectroscopy (XPS), Brunauer-Emmett-Teller (BET) and Transmission Electron Microscopy (TEM). The results show that as the Pd content increases, the adsorbed oxygen content further increases, but at the same time Pd⁰ will agglomerate and lose some active sites, which will affect its catalytic performance. While 0.2%Pd@UIO-66 has the highest concentration of Pd⁰, the result shows it has the best catalytic activity and the T₉₀ temperature is 210 °C.

This paper introduces a novel method for preparing high-performance, metal-containing carbon foam wave-absorbing materials. The process involves foaming glucose through catalysis by transition metals followed by high-temperature pyrolysis. The resulting carbon foam materials exhibit a highly porous structure, which is essential for their wave-absorption properties. Notably, at a thickness of 2.0 mm, the glucose-derived carbon foam composite catalyzed by Fe and Co (GCF-CoFe) achieved a minimum reflection loss (RL_min) of −51.4 dB at 15.11 GHz, along with an effective absorption bandwidth (EAB) of 5.20 GHz, spanning from 12.80 GHz to 18.00 GHz. These impressive performance metrics indicate that this approach offers a promising pathway for developing low-density, efficient carbon foam materials for wave-absorption applications. This advancement has significant implications for fields requiring effective electromagnetic interference (EMI) shielding, stealth technology, and other related applications, potentially leading to more efficient and lightweight solutions.