Herein, we report the performances of crosslinked facilitated transport membranes based on carboxymethylated nanofibrils of cellulose (cmNFC) and polyvinylamine (PVAm) with the use of 3-(2-Aminoethylamino) propyltrimethoxysilane (AEAPTMS) as second fixed carrier for CO₂ selectivity and permeability. The grafting of AEAPTMS on cmNFC was optimized by following the hydrolysis/condensation kinetics by ²⁹Si Nuclear Magnetic Resonance (NMR) analyses and two different strategies of the process of membrane production were investigated. In optimized conditions, around 25% of the -COOH functions from cmNFC have crosslinked with PVAm. The crosslinked membranes were less sensitive to liquid water and the crystallinity of PVAm was tuned by the conditions of the membrane elaboration. In both processes, CO₂ selectivity and permeability were enhanced especially at high water vapor concentration by the use of PVAm and AEAPTMS suggesting the existence of a facilitation effect due to amine-CO₂ interaction, while the mechanical integrity of the swollen membranes remained intact.

Among solution-processable metal oxides, zinc oxide (ZnO) nanoparticle inks are widely used in inverted organic solar cells for the preparation, at relatively low temperatures (<120 °C), of highly efficient electron-transporting layers. There is, however, a recent interest to develop more sustainable and less impacting methods/strategies for the preparation of ZnO NPs with controlled properties and improved performance. To this end, we report here the synthesis and characterization of ZnO NPs obtained using alternative reaction solvents derived from renewable or recycled sources. In detail, we use (i) recycled methanol (r-MeOH) to close the loop and minimize wastes or (ii) bioethanol (b-EtOH) to prove the effectiveness of a bio-based solvent. The effect of r-MeOH and b-EtOH on the optical, morphological, and electronic properties of the resulting ZnO NPs, both in solution and thin-films, is investigated, discussed, and compared to an analogous reference material. Moreover, to validate the properties of the resulting materials, we have prepared PTB7:PC₇₁BM-based solar cells containing the different ZnO NPs as a cathode interlayer. Power conversion efficiencies comparable to the reference system (≈7%) were obtained, validating the proposed alternative and more sustainable approach.