Emerging technologies, such as portable electronics, have had a huge impact on societal norms, such as access to real time information. To perform these tasks, portable electronic devices need more and more accessories for the processing and dispensation of the data, resulting in higher demand for energy and power. To overcome this problem, a low cost high-performing flexible fiber shaped asymmetric supercapacitor was fabricated, exploiting 3D-spinel manganese oxide Mn₃O₄ as cathode and 2D molybdenum disulfide MoS₂ as anode. These asymmetric supercapacitors with stretched operating voltage window of 1.8 V exhibit high specific capacitance and energy density, good rate capability and cyclic stability after 3000 cycles, with a capacitance retention of more than 80%. This device has also shown an excellent bending stability at different bending conditions.

A simple, low cost, and “green” method of hydrothermal synthesis, based on the addition of l-ascorbic acid (l-AA) as a reducing agent, is presented in order to obtain reduced graphene oxide (rGO) and hybrid rGO-MoO₂ aerogels for the fabrication of supercapacitors. The resulting high degree of chemical reduction of graphene oxide (GO), confirmed by X-Ray Photoelectron Spectroscopy (XPS) analysis, is shown to produce a better electrical double layer (EDL) capacitance, as shown by cyclic voltammetric (CV) measurements. Moreover, a good reduction yield of the carbonaceous 3D-scaffold seems to be achievable even when the precursor of molybdenum oxide is added to the pristine slurry in order to get the hybrid rGO-MoO₂ compound. The pseudocapacitance contribution from the resulting embedded MoO₂ microstructures, was then studied by means of CV and electrochemical impedance spectroscopy (EIS). The oxidation state of the molybdenum in the MoO₂ particles embedded in the rGO aerogel was deeply studied by means of XPS analysis and valuable information on the electrochemical behavior, according to the involved redox reactions, was obtained. Finally, the increased stability of the aerogels prepared with l-AA, after charge-discharge cycling, was demonstrated and confirmed by means of Field Emission Scanning Electron Microscopy (FESEM) characterization.

Nanostructured materials possess unique physical-chemical characteristics and have attracted much attention, among others, in the field of energy conversion and storage devices, for the possibility to exploit both their bulk and surface properties, enabling enhanced electron and ion transport, fast diffusion of electrolytes, and consequently high efficiency in the electrochemical processes. In particular, titanium dioxide received great attention, both in the form of amorphous or crystalline material for these applications, due to the large variety of nanostructures in which it can be obtained. In this paper, a comparison of the performance of titanium dioxide prepared through the oxidation of Ti foils in hydrogen peroxide is reported. In particular, two thermal treatments have been compared. One, at 150 °C in Ar, which serves to remove the residual hydrogen peroxide, and the second, at 450 °C in air. The material, after the treatment at 150 °C, results to be not stoichiometric and amorphous, while the treatment at 450 °C provide TiO₂ in the anatase form. It turns out that not-stoichiometric TiO₂ results to be a highly stable material, being a promising candidate for applications as high power Li-ion batteries, while the anatase TiO₂ shows lower cyclability, but it is still promising for energy-storage devices.

Graphene is a 2D carbon material with peculiar features such as high electrical conductivity, high thermal conductivity, mechanical stability, and a high ratio between surface and thickness. Applications are continuously growing, and the possibility of dispersing graphene in low-boiling green solvents could reduce its global environmental impact. Pristine graphene can be dispersed in high concentration only in polar aprotic solvents that usually have high boiling points and high toxicity. For this reason, the oxidized form of graphene is always used, as it is easier to disperse and to subsequently reduce to reduced graphene oxide. However, compared to pristine graphene, reduced graphene oxide has more defects and has inferior properties respect to graphene. In this work, the polymerization of (diethyl maleate derivate) on graphene obtained by sonication was performed in a microwave reactor. The obtained material has good stability in ethanol even after a long period of time, therefore, it can be used to deposit graphene by mass production of inks or by casting and easy removal of the solvent. The thermal annealing by heating at 300–400 °C in inert atmosphere allows the removal of the polymer to obtain pristine graphene with a low number of defects.