Polypropylene (PP), as a general thermoplastic polymer, is broadly used in different fields. However, the high flammability, melt dripping and poor mechanical properties of PP are a constraint to the expansion of its applications. In this paper, PP composites containing a combination of a phenethyl-bridged DOPO derivative (PN-DOPO) and organic montmorillonite (OMMT) were prepared via melt blending. The synergistic effects of PN-DOPO and OMMT on the flame retardancy, thermal stability and mechanical properties of PP composites were investigated systematically. The results showed that 20 wt% addition of PN-DOPO with OMMT improved the flame retardancy of PP composites. In particular, the introduction of 17 wt% PN-DOPO and 3 wt% OMMT increased the LOI values of the PP matrix from 17.2% to 23.6%, and the sample reached the V-0 level and reduced the heat release rate and total heat release. TGA indicated that OMMT could improve the thermal stability of the PP/PN-DOPO blends and promote the char residues of PP systems. Rheological behaviour showed a higher storage modulus, loss modulus and complex viscosity of PP/PN-DOPO/OMMT composites, suggesting a more effective network structure. In addition, the tensile strength, flexural properties and impact strength of the PP/PN-DOPO/OMMT composites actually increased for a good dispersion effect. Combined with the char layer analysis, the introduction of OMMT promoted more continuous and compact structural layers containing an aluminium–silicon barrier and phosphorus-containing carbonaceous char in the condensed phase. OMMT can improve the flame retardancy, thermal stability and mechanical properties of PP, and, thus, PN-DOPO/OMMT blends can serve as an efficient synergistic system for flame-retarded PP composites.

Aluminum phosphates coated sepiolite nanocomposite was fabricated via a simple one-pot heterogeneous precipitation strategy, and the effects of aluminum phosphates on the morphology of aluminum phosphates coated sepiolite were investigated. Moreover, the effect of aluminum phosphates coated sepiolite on the flame-retardant behavior, mechanical properties, and thermal stability of epoxy resin have been discussed. The results indicated that the introduction of only 20 wt% aluminum phosphates coated sepiolite in epoxy resin increased the limited oxygen index from 21.8% to 30.1%, thus the material met the UL-94 V-0 rating. Thermogravimetric analyses revealed that char yield increased in the presence of aluminum phosphates coated sepiolite form thermally stable carbonaceous char. Aluminum phosphates–coated sepiolite could improve the mechanical performance, thermal stability of epoxy resin.

To improve the poor impact toughness of polypropylene (PP), organo-sepiolite (O-Sep) filled 80/20 (w/w) polypropylene/poly(acrylonitrile-butadiene-styrene) (PP/ABS) nanocomposites were fabricated. The contents of O-Sep were correlated with the morphological, mechanical, and rheological behavior of PP/ABS/O-Sep blends. Scanning electron microscopy (SEM) was applied to study the morphology and thermogravimetric analysis (TGA) was applied to study the thermal stability. Differential scanning calorimetry (DSC) and X-ray diffraction (XRD) were applied to study the crystallinity. The obtained results show that O-Sep enhanced the dispersion of ABS in the PP matrix and increased the crystallinity of blends. The rheological results show that O-Sep could increase the viscosity, storage modulus, and loss modulus of blends. Moreover, the mechanical behavior shows that O-Sep (at proper content) simultaneously increased the tensile modulus, flexural modulus, and impact strength of PP/ABS/O-Sep blends.

Polymer blending has been widely used to fabricate polymeric films in the last decade due to its superior properties to a single component. In this study, an aluminum phosphate-coated halloysite nanotube (HNTs@AlPO₄) was fabricated using a one-pot heterogeneous precipitation method, organically modified HNTs@AlPO₄ (o-HNTs@AlPO₄) was used to improve the performance of polyethylene oxide/poly(butylene adipate-co-terephthalate) (PEO/PBAT) blends, and the mechanical and rheological properties of the PEO/PBAT/o-HNTs@AlPO₄ films were systematically discussed. According to our results, there is an optimal addition for adequate AlPO₄ nanoparticle dispersion and coating on the surface of HNTs, and organic modification could improve the interfacial compatibility of HNTs@AlPO₄ and the polymeric matrix. Moreover, o-HNTs@AlPO₄ may serve as a compatibilizer between PEO and PBAT, and PEO/PBAT/o-HNTs@AlPO₄ films have better mechanical and rheological properties than the PEO/PBAT blends without the o-HNTs@AlPO₄ component.

Incorporating a 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide-based derivative (1,4-bis(diphenoxyphosphoryl)piperazine, DIDOPO) in combination with modified calcium sulfate whiskers (MCSWs) improved the flame retardancy, thermal stability, and rheological properties of a polyethylene oxide (PEO) composite. The synergistic flame-retardant effect of DIDOPO and MCSW on the PEO system was investigated. After introducing 5 wt.% MCSW and 10 wt.% DIDOPO into PEO, the UL-94 rating of the composite reached V-0, and the limiting oxygen index was increased to 26.5%. Additionally, the peak and average heat release rates and total heat release of the PEO/10% DIDOPO/5% MCSW composite decreased by 38.9%, 22%, and 20.07%, respectively. The results of a thermogravimetric analysis (TGA) revealed that PEO/10% DIDOPO/5% MCSW displayed an improved initial thermal stability and rate of char formation compared to those of the PEO matrix. The results of TGA/Fourier transform infrared analysis indicated that the composites exhibited phosphorus-containing groups during thermal degradation, based on the characteristic absorption peaks, and increased amounts of gas-phase volatiles. The morphologies and structures of the residues indicated that the PEO/10% DIDOPO/5% MCSW blend was less stable than PEO during combustion. The MCSW mixture formed a denser, more continuous carbon layer on the composite surface during combustion. The rheological behavior indicated that the high complex viscosity and moduli of PEO/10% DIDOPO/5% MCSW promoted the cross-linking network structure of the condensed phase during combustion. MCSW exhibited an excellent flame retardancy and improved thermal stability, which are potentially promising for use in fire safety applications.