Five Co-modified P92-type steels with different contents of Cr, W, Mo, B, N, and Re have been examined to evaluate the effect of the chemical composition on the evolution of Laves phase during creep at 650 °C. The creep tests have been carried out at 650 °C under various applied initial stresses ranging from 80 to 200 MPa until rupture. An increase in the B and Cr contents leads to a decrease in the size and volume fraction of M₂₃C₆ carbides precipitated during tempering and an increase in their number particle density along the boundaries. In turns, this affects the amount of the nucleation sites for Laves phase during creep. The (W+Mo) content determines the diffusion growth and coarsening of Laves phase during creep. Susceptibility of Laves phase to coarsening with a high rate is caused by the large difference in Gibbs energy between fine and large particles located at the low-angle and high-angle boundaries, respectively, and can cause the creep strength breakdown. The addition of Re to the 10%Cr steel with low N and high B contents provides the slowest coarsening of Laves phase among the steels studied.

The effect of tempering after water quenching on the strength and fracture toughness of two steels with chemical compositions of 0.34%C-1.77%Si-1.35Mn-0.56%Cr-0.2%Mo-0.04%Nb-0.03Ti-0.002B and 0.44%C-1.81%Si-1.33%Mn-0.82%Cr-0.28%Mo was examined. The last steel exhibits quenching embrittlement in an as-quenched condition. At a tempering temperature of 280 °C, the precipitation of transition η–Fe₂C carbides in martensitic matrix leads to increasing fracture toughness and eliminates quench embrittlement in the steel with 0.44 wt.%C. Tempered martensite embrittlement at 400 °C appears as decreased values of the Charpy V-notch impact energy, ductility and the product of strength and elongation, σ_B×δ (MPa×%) and is attributed to increased effective grain size for fracture, mainly. The precipitation of boundary cementite takes place at tempering at 500 °C and provides increased ductility and fracture toughness despite a decohesion along carbide/ferrite interfaces. The low severity of TME in Si-rich low-alloy medium carbon steels is attributed to the suppression of boundary cementite precipitation at tempering temperatures ≤400 °C.