Supramolecular polymers are widely utilized and applied in self-assembly or self-healing materials, which can be repaired when damaged. Normally, the healing process is classified into two types, including extrinsic and intrinsic self-healable materials. Therefore, the aim of this work is to review the intrinsic self-healing strategy based on supramolecular interaction or non-covalent interaction and molecular recognition to obtain the improvement of mechanical properties. In this review, we introduce the main background of non-covalent interaction, which consists of the metal–ligand coordination, hydrogen bonding, π–π interaction, electrostatic interaction, dipole–dipole interaction, and host–guest interactions, respectively. From the perspective of mechanical properties, these interactions act as transient crosslinking points to both prevent and repair the broken polymer chains. For material utilization in terms of self-healing products, this knowledge can be applied and developed to increase the lifetime of the products, causing rapid healing and reducing accidents and maintenance costs. Therefore, the self-healing materials using supramolecular polymers or non-covalent interaction provides a novel strategy to enhance the mechanical properties of materials causing the extended cycling lifetime of products before replacement with a new one.

Polymer foams are an important class of engineering material that are finding diverse applications, including as structural parts in automotive industry, insulation in construction, core materials for sandwich composites, and cushioning in mattresses. The vast majority of these manufactured foams are homogeneous with respect to porosity and structural properties. In contrast, while cellular materials are also ubiquitous in nature, nature mostly fabricates heterogeneous foams, e.g., cellulosic plant stems like bamboo, or a human femur bone. Foams with such engineered porosity distribution (graded density structure) have useful property gradients and are referred to as functionally graded foams. Functionally graded polymer foams are one of the key emerging innovations in polymer foam technology. They allow enhancement in properties such as energy absorption, more efficient use of material, and better design for specific applications, such as helmets and tissue restorative scaffolds. Here, following an overview of key processing parameters for polymer foams, we explore recent developments in processing functionally graded polymer foams and their emerging structures and properties. Processes can be as simple as utilizing different surface materials from which the foam forms, to as complex as using microfluidics. We also highlight principal challenges that need addressing in future research, the key one being development of viable generic processes that allow (complete) control and tailoring of porosity distribution on an application-by-application basis.

This research aims to utilize sericin, which is the waste from boiling silk cocoon, for the supramolecular scaffold preparation with chitosan. A suitable method for the self-assembled scaffold formation of sericin and chitosan at 1:1 stoichiometry is presented and the morphological and physical properties of the scaffold are studied. The effect of an alcohol/NaOH solution on the secondary structure of sericin protein within the sericin-chitosan scaffold, with adjusted pH, was investigated. Additionally, the scaffold was tested in a native phosphate buffer solution (PBS). The results show that sericin increases the porosity of scaffold while chitosan increases the rigidity. The self-assembled sericin and chitosan material is nontoxic to human cells and which can adhere and spread well on such support. For the effect of the molecular weight of chitosan (15,000 and 100,000 g/mol), the scaffold made from lower molecular weight (MW) chitosan provides a somewhat smaller porosity, but a similar swelling ratio and water uptake. On the basis of this research, sericin, which is a silk waste from the textile industry, can be utilized to produce a self-assembled scaffold with chitosan in order to increase the porosity of the scaffold. This type of scaffold is not toxic and can be used for the adhesion of fibroblast cells.

Natural rubber foam (NRF) can be prepared from concentrated natural latex, providing specific characteristics such as density, compression strength, compression set, and so on, suitable for making shape-memory products. However, many customers require NRF products with a low compression set. This study aims to develop and prepare NRF to investigate its recoverability and other related characteristics by the addition of charcoal and silica fillers. The results showed that increasing filler loading increases physical and mechanical properties. The recoverability of NRF improves as silica increases, contrary to charcoal loading, due to the higher specific surface area of silica. Thermodynamic aspects showed that increasing filler loading increases the compression force (F) as well as the proportion of internal energy to the compression force (F_u/F). The entropy (S) also increases with increasing filler loading, which is favorable for thermodynamic systems. The activation enthalpy (∆H_a) of the NRF with silica is higher than the control NRF, which is due to rubber–filler interactions created within the NRF. A thermodynamic concept of crosslinked rubber foam with filler is proposed. From theory to application, in this study, the NRF has better recoverability with silica loading.

Calcium carbonate (CaCO₃) is one of the most important inorganic powders and is widely used as filler in order to reduce costs in the rubber industry. Nanocalcium carbonate reduces costs and acts as a semireinforcing filler that improves the mechanical properties of rubber composites. The objective of this study was to investigate the effect of nano-CaCO₃ (NCC) and micro-CaCO₃ (MCC) on the properties of natural rubber composites, in particular, new results of structure–properties relationship. The effects of NCC/MCC on the properties of rubber composites, such as Mooney viscosity, bound rubber, Mullins effect, and Payne effect, were investigated. The result of the Mullins effect of rubber composites filled with NCC was in good agreement with the results of Mooney viscosity and bound rubber, with higher Mooney viscosity and bound rubber leading to higher stress to pull the rubber composites. The Payne effect showed that the value of different storage moduli (ΔG’) of rubber composites filled with 25 parts per hundred rubber (phr) NCC was the lowest due to weaker filler network, while the rubber supplemented with 100 phr NCC had more significant ΔG’ values with increase in strain. The results of rubber composites filled with MCC showed the same tendency as those of rubber composites filled with NCC. However, the effect of specific surface area of NCC on the properties of rubber composites was more pronounced than those of rubber composites filled with MCC. Finite element analysis of the mechanical property of rubber composites was in good agreement with the result from the experiment. The master curves of time–temperature superposition presented lower free volume in the composites for higher loading of filler, which would require more relaxation time of rubber molecules. This type of nanocalcium carbonate material can be applied to tailor the properties and processability of rubber products.