In this study, the effect of oxygen in the shielding gas on the material flow behavior of the weld pool surface was discussed to clarify the dominant driving weld pool force in keyhole plasma arc welding (KPAW). To address this issue, the convection flow on the top surface of weld pool was observed using a high-speed video camera. The temperature distribution on the surface along keyhole wall was measured using the two-color pyrometry method to confirm the Marangoni force activity on the weld pool. The results show that the inclination angle of the keyhole wall (keyhole shape) increased especially near the top surface due to the decrease in the surface tension of weld pool through surface oxidation when a shielding gas of Ar + 0.5% O₂ was used. Due to the change in the keyhole shape, the upward and backward shear force compositions created a large inclination angle at the top surface of the keyhole. From the temperature measurement results, the Marangoni force was found to alter the direction when 0.5% O₂ was mixed with the shielding gas. The shear force was found to be the strongest force among the four driving forces. The buoyant force and Lorentz force were very weak. The Marangoni force was stronger than the Lorentz force but was weaker than shear force. The interaction of shear force and Marangoni force controlled the behavior and speed of material flow on the weld pool surface. A strong upward and backward flow was observed in the case of mixture shielding gas, whereas a weak upward flow was observed for pure Ar. The heat transportation due to the weld pool convection significantly changed when only a small amount of oxygen was admixed in the shielding gas. The results can be applied to control the penetration ratio in KPAW.

Nonwoven fabrics are widely used in the textile manufacturing industry due to their advanced characteristics, such as their soft, water-repellent, recycle, ecological, and resilient functions. Nowadays, one of the innovated technologies applied to bond nonwoven fabrics is the ultrasonic welding method, due to the advantages afforded by its clean, fast, and reliable approach. In this work, isotactic polypropylene (PP) nonwoven fabrics were bonded by a continuous ultrasonic welding process. In order to consider the influence of the roller on the formation of welding joints and their mechanical properties, different roller profiles were designed, fabricated, and tested. Eight types of roller profiles corresponding to No. 1–No. 8 in the experiments were divided into four groups. After bonding, the microstructure in a typical case (i.e., No. 1) was captured by scanning electron microscopy (SEM) to examine the formation of the welding joints. Additionally, the load and the peel strength of the welding joints of all eight roller profiles were analyzed. The results showed that no welding defects, such as cracks or blowholes, were visible in the melted zone. The load depended on the area ratio(s) of the welding area (S₀) to the cycling area (S₁). Furthermore, it was found out that the peel strength of the welding joints with brick structures were higher than the peel strength in the case of solid line structures.

This paper aims to develop a novel tungsten inner gas (TIG) welding torch in order to join thin sheets efficiently. Using a narrowing nozzle (constricted nozzle) inside a conventional TIG torch can critically improve the position accuracy of the tungsten electrode and also the arc plasma characteristics and heat input density. In order to evaluate the efficiency of this new torch, weld bead appearance and cross-section images were examined by an optical microscope, scanning electron microscope (SEM), and electron back scatter diffraction patterns (EBSD). The results showed that in all cases, the weld bead profile was stable without undercut and burn-through. Full penetration weld was seen. The width of weld bead on the bottom surface was increased much in comparison to conventional TIG welding. However, the results from SEM and EBSD images indicated that in the case of low welding current, the blowholes were found out on the side of the thinner material (SS400). The penetration of SUS430 material to SS400 material was not good. It seems that no fusion of SUS430 material to SS400 at the bottom surface can be seen. Meanwhile, no blowholes were seen in the case of high welding current. The penetration was better, and the fusion was reached on the bottom surface.