A diode-side-pumped, high-energy, high-beam-quality, pulsed solid-state Nd³⁺:Y₃Al₅O₁₂ (Nd:YAG) laser with a thermoelectric cooler (TEC) is investigated in this study. The pump laser was a pulsed laser diode array with maximum peak power of 15 kW. A 350 mJ laser pulse was obtained with a wavelength of 1064 nm, a pulse duration of 10 ns, a total electrical-to-optical efficiency of 7.5%, a relative stability of output energy of 5%, and a beam quality of M² < 4.

Lithium niobate material (LN) has shown great application potentials in the fabrication of integrated optical devices due to its excellent physical properties, especially with the occurrence of lithium niobate-on-insulator (LNOI) substrate. However, the greatest challenge of micro/nano optical devices based on LN material lies in the precise etching process and thus limits its applications. In this paper, we comprehensively analyze the etching results treated by the proposed proton-exchanged wet-etching method (PEWE) combining with theoretical simulations and experiments. It is found that the proton-exchanged layer in the LN material can be easily etched after using a mixture acid of HF/HNO₃, leading to the improvement of etching rate and surface morphology. The lowest roughness of the optical waveguide is measured to be 0.81 nm, which is beneficial for the performance improvement of LN-based optical devices. Ultimately, a quasi-vertical sidewall of the upper part of optical waveguide with improved surface morphology is successfully realized by utilizing the PEWE. Moreover, this method could also be extended to improve the performance of LNOI-based optical devices and pave the way for ultra-compact photonic integrated circuits based on LNOI.

Additively manufactured tungsten and its alloys have been widely used for plasma facing components (PFCs) in future nuclear fusion reactors. Under the fusion process, PFCs experience a high-temperature exposure, which will ultimately affect the microstructural features, keeping in mind the importance of microstructures. In this study, microhardness and electron backscatter diffraction (EBSD) techniques were used to study the specimens. Vickers hardness method was used to study tungsten under different parameters. EBSD technique was used to study the microstructure and Kikuchi pattern of samples under different orientations. We mainly focused on selective laser melting (SLM) parameters and the effects of these parameters on the results of different techniques used to study the behavior of samples.