In this work, the effect of modified graphene oxide and polytetrafluoroethylene (PTFE) on the tribological and anticorrosion properties of waterborne polyurethane (WPU) was studied. The modified graphene oxide (MGO) was obtained by the surface functionalization modification of graphene oxide (GO) with isophorone diisocyanate (IPDI), and MGO/WPU composite coating and MGO-PTFE/WPU composite coating with different mass fractions of MGO were prepared. The tribological and electrochemical experiment results demonstrated that the tribological properties of the coating and the corrosion resistance of the worn coating were effectively enhanced under the synergistic effect of MGO and PTFE. Finally, a mechanism was proposed to explain the improvement in anticorrosion performance of the worn coating.

SiO₂/ZrO₂ and SiO₂/ZrO₂/Al₂O₃ composite organic–inorganic coatings were prepared by the sol-gel technology. The structure of the coating was characterized by IR, particle size analyzer, SEM, and AFM, respectively. The results showed that ZrO₂, SiO₂ (inorganic component), and siloxane had undergone a hydrolytic condensation reaction, and the composite organic–inorganic coatings were formed with -O-M-O- (M is Si, Zr) as molecular skeleton network structure. Adding an appropriate ratio of ZrO₂ sol, no agglomeration and phase separation occurred, which could significantly improve the refractive index, hardness, and light transmittance of the coatings. Al₂O₃ sol could greatly improve the friction resistance of the composite organic–inorganic coatings, and the Bayer ratio of the composite coatings could reach 7.86. By adjusting the proportioning of composite sol solution, the refractive index of the composite transparent coatings could be controlled from 1.52 to 1.65.