Flaxseed oil (FO) is composed mainly of polyunsaturated fatty acids that are very sensitive to oxidation induced by oxygen, temperature, and light. To overcome this problem, gelatin-based films containing glucose are crosslinked via the Maillard reaction (MR) at 120 °C and used for the conception of pouches in which the FO was packaged. The prepared pouches, as well as the oil alone, are incubated at 50 °C for 21 days. The results show that the peroxide index of the oil stored in the gelatin-based pouches is almost stable and decreases on the 21st day. The specific extinction coefficients prove a more pronounced degradation of the non-package oil (control). In addition, the results of thiobarbituric acid reactive substances (TBARs) test reveal higher values in the control, with a tendency to continuously increase up until the 21st day. However, the oil stored in the pouches reveals less TBARs content, decreasing with oxidation time. The non-heated glucose-supplemented pouches showed the best results, suggesting a moderate and gradual development of the MR at 50 °C. The application of pouches based on gelatin films seems to be an effective and interesting tool for protecting FO against lipid oxidation, acting as perfectly biodegradable and sustainable containers for small doses.

The study focused on the elaboration and the characterization of blend biofilms based on European eel skin gelatin (ESG) and protein isolate (EPI) and the assessment of European oil (EO) incorporation effect on their properties. Data displayed that the incorporation of EPI and EO to the gelatin formulation decreased the lightness and yellowness of composite and emulsified films, respectively, compared to ESG film. Moreover, ESG films exhibited improved mechanical properties than EPI films. FTIR analysis, all incorporated films with EO at the ratio 1:4 (oil/polymer) revealed similar characteristic bands as in free-oil films. Further, the SEM images of 100% ESG and 100% EPI films showed a smooth and homogenous structure, whereas the cross-section of blend film (at a ratio 50:50) displayed a rougher microstructure. In addition, emulsified film ESG100 revealed a smooth and homogeneous microstructure compared to that prepared using EPI/ESG 50/50 ratio. Furthermore, EPI or EO addition into the ESG matrix enhanced the blend films antioxidant activities.